Effect of wood moisture content and adhesive open time on the adhesion strength of wet bonded Pinus radiata wood

被引：0
|
作者：
Favis, Jesse [1 ]
Balboni, Bruno Monteiro [1 ]
Wessels, C. Brand [1 ]
机构：
[1] Stellenbosch Univ, Dept Forest & Wood Sci, Stellenbosch, South Africa
来源：
EUROPEAN JOURNAL OF WOOD AND WOOD PRODUCTS | 2024年 / 82卷 / 02期
关键词：
Bond strength (materials) - Glues - Gluing - Moisture - Moisture determination;
D O I：
10.1007/s00107-024-02050-w
中图分类号：
S7 [林业];
学科分类号：
0829 ; 0907 ;
摘要：
Gluing wood in the wet state can reduce warping, splitting, and increase processing volume recovery. Adhesive open time and moisture content may play an important role in bond line strength, but there are no specifications for wet wood bonding. Wood specimens at two different moisture contents were glued with three polyurethane adhesives and tested in shear on the bond line. Open time of 15 min was superior to 4 and 40 min. All adhesives performed better when wood was glued at 30% moisture content than at 101%, but only the 15- and 40-min open time met the minimum shear requirement.
引用
收藏
页码：557 / 560
页数：4
相关论文
共 50 条
  • [1] Effect of wood moisture content and adhesive open time on the adhesion strength of wet bonded Pinus radiata wood
    Jesse Favis
    Bruno Monteiro Balboni
    C. Brand Wessels
    European Journal of Wood and Wood Products, 2024, 82 : 557 - 560
  • [2] Adhesive strength and micromechanics of wood bonded at different moisture contents
    Tran, Anita
    Konnerth, Johannes
    Gindl-Altmutter, Wolfgang
    INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES, 2024, 132
  • [3] Effect of open assembly time and equilibrium moisture content on the penetration of polyurethane adhesive into thermally modified wood
    Bastani, Alireza
    Adamopoulos, Stergios
    Militz, Holger
    JOURNAL OF ADHESION, 2017, 93 (07): : 575 - 583
  • [4] Effect of wood moisture content on adhesion of varnish coatings
    Sonmez, Abdullah
    Budakci, Mehmet
    Bayram, Mehmet
    SCIENTIFIC RESEARCH AND ESSAYS, 2009, 4 (12): : 1432 - 1437
  • [5] Characterizing Moisture Content and Gradients in Pinus radiata Soft Wood Using Electrical Impedance Spectroscopy
    Chilcott, Terry C.
    Halimanto, Dewi
    Langrish, Tim A. G.
    Kavanagh, John M.
    Coster, Hans G. L.
    DRYING TECHNOLOGY, 2011, 29 (01) : 1 - 9
  • [6] THE VARIATION OF BARK WOOD BOND STRENGTH WITH MOISTURE-CONTENT OF PINUS-RADIATA AND 3 EUCALYPT SPECIES DURING STORAGE
    MOORE, GA
    AUSTRALIAN FOREST RESEARCH, 1987, 17 (01): : 73 - 78
  • [7] Influence of Moisture Content on the Bond Strength and Water Resistance of Bonded Wood Joints
    Bomba, Jan
    Sedivka, Premysl
    Boehm, Martin
    Devera, Michal
    BIORESOURCES, 2014, 9 (03): : 5208 - 5218
  • [8] RESIN AND FATTY ACID CONTENT OF LIVING PINUS RADIATA WOOD
    PORTER, LJ
    NEW ZEALAND JOURNAL OF SCIENCE, 1969, 12 (04): : 687 - &
  • [9] Adhesive strength and micromechanics of wood bonded at low temperature
    Tran, Anita
    Mayr, Melanie
    Konnerth, Johannes
    Gindl-Altmutter, Wolfgang
    INTERNATIONAL JOURNAL OF ADHESION AND ADHESIVES, 2020, 103
  • [10] Effect of autohydrolysis on Pinus radiata wood for hemicellulose extraction
    Santos, Tamara M.
    Virginia Alonso, M.
    Oliet, Mercedes
    Dominguez, Juan C.
    Rigual, Victoria
    Rodriguez, Francisco
    CARBOHYDRATE POLYMERS, 2018, 194 : 285 - 293
12345