Performance of natural product-based materials as adhesives in the fabrication of mangrove wood composites

Biodegradable adhesives prepared using three different forms of soy protein-based products (defatted soy flour/soy protein concentrate/soy protein isolate), sodium hydroxide, and itaconic acid polyamidoamine-epichlorohydrin (IA-PAE) with 0 wt%-20 wt% substitution rates were utilized to enhance the production of mangrove wood composites. 1H nuclear magnetic reso-nance, differential scanning calorimetry, and ultra-high-resolution field emission scanning elec-tron microscopy were employed to characterize the composite samples. Other measurements involved the determination of viscosity, pH, physical, mechanical, dimensional stability, CT numbers, and relative electron density parameters. The ideal curing conditions for the composite bio-adhesives were found to be 15 wt% IA-PAE, 602.50 +/- 172.21-391.11 +/- 105.82 mPa s, pH 11.0, 180 degrees C, and 18 min, respectively. The improved physiochemical characteristics of DSF, SPC, and SPI confirmed that NaOH/IA-PAE was integrated into the adhesive system and ameliorated the overall performance of the resulting composites. The results showed that all composite samples, except for those bonded with 0 wt% and 5 wt% IA-PAE, matched up with the quality specification stated in the JIS A-5908 and ASTM D1037. Samples D1, D2, and D3 exhibited op-timum characteristics, demonstrating their uses in the development of low-toxicity and sustain-able reference tissue substitute phantom in radiological areas.