The Oxidation Behaviors of NiCoCrAlY Coatings After Pre-Oxidation Treatment During High-Temperature Oxidation at 800 degree celsius and 900 degree celsius

Thermal barrier coatings (TBCs) are essential for protecting the high-temperature components in gas turbines. However, the durability of TBCs is limited, and new technologies to improve their lifetime are necessary. This study focuses on the pre-oxidation treatment of the NiCoCrAlY bond coat in TBCs to reduce the growth rate of the thermally grown oxide (TGO) and improve the TBC lifetime. The mechanism of the TGO growth rate reduction by the pre-oxidation treatment of NiCoCrAlY was investigated. Oxidation behaviors of the surface of NiCoCrAlY coating samples with or without pre-oxidation treatment were evaluated in air at 800 degree celsius and 900 degree celsius. In-situ X-ray diffraction (XRD) measurements and isothermal oxidation tests were performed. The obtained results revealed that the growth rate of TGO is significantly suppressed by alpha-Al(2)O(3 )layer formed by the pre-oxidation treatment. The generation of gamma-Al2O3 and theta-Al2O3, which are typically formed below 900 degree celsius, was significantly reduced by pre-oxidation. It is suggested that this reduction suppresses of the TGO growth.