Preparation of a Microwave-Absorbing UV Coating Using a BaFe12O19-Polypyrrole Nanocomposite Filler

BaFe12O19-polypyrrolenanocomposites were prepared via the in situ chemical oxidative polymerization of pyrrole monomers in the presence of BaFe12O19 powder, with ammonium persulfate as an oxidant and sodium dodecyl benzene sulfonate as a dopant. X-ray diffraction measurements and Fourier-transform infrared spectroscopy indicated that there were no chemical interactions between BaFe12O19 and polypyrrole. In addition, scanning electron microscopy showed that the composites exhibited a core-shell structure. Subsequently, the prepared nanocomposite was used as a filler to prepare a coating suitable for ultraviolet curing. The performance of the coating was investigated by evaluating its hardness, adhesion, absorbance, and resistance to acids and alkalis. Importantly, the addition of BaFe12O19-polypyrrole nanocomposites not only improved the coating hardness and adhesion but also produced a coating with a good microwave absorption performance. The results suggested that BaFe12O19/PPy composite has a lower reflection loss peak and a larger effective bandwidth at the X band when the proportion of the absorbent sample is 5-7%, when the absorption performance is the best. The reflection loss is in the range of 8.88-10.92 GHz below -10 dB.