Effect of micro-galvanic corrosion on corrosion fatigue cracking of the weld joint of high strength bridge steel

被引：9
|
作者：
Li, Qi [1 ]
Yao, Qiong [2 ]
Sun, Liyang [1 ]
Ma, Hongchi [1 ]
Zhang, Chuang [2 ]
Wang, Ning [2 ]
机构：
[1] Univ Sci & Technol, Inst Adv Mat & Technol, Natl Mat Corros & Protect Data Ctr, Key Lab Corros & Protect MOE, Beijing 100083, Peoples R China
[2] Xichang Satellite Launch Ctr, Xichang 615000, Sichuan, Peoples R China
来源：
INTERNATIONAL JOURNAL OF FATIGUE | 2023年 / 170卷
基金：
中国国家自然科学基金;
关键词：
High-strength bridge steel; Marine atmosphere; Local electrochemical technique; Micro-galvanic corrosion; Corrosion fatigue failure; SCANNING KELVIN PROBE; E690; STEEL; FORCE MICROSCOPY; GROWTH-BEHAVIOR; CR; MICROSTRUCTURE;
D O I：
10.1016/j.ijfatigue.2023.107568
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
The local electrochemical and corrosion fatigue cracking behavior of the weld joint of Q690qE high-strength bridge steel was investigated in simulated marine environment. It reveals the weld joint was vulnerable to corrosion fatigue failure in polluted marine atmosphere with the corrosion fatigue life considerably lower than that of parent metal. The micro-galvanic corrosion effect between CGHAZ and WM played a dominant role in the corrosion fatigue failure of the weld joint, leading to the final fracture mostly at CGHAZ. The micro-galvanic corrosion was caused by Volta potential variation among various subzones, which was evidenced by local electrochemical techniques.
引用
收藏
页数：15
相关论文
共 50 条
  • [21] Micro-galvanic corrosion corrosion of Cu/Ru couple in potassium periodate (KIO4) solution
    Cheng, Jie
    Pan, Jinshan
    Wang, Tongqing
    Lu, Xinchun
    CORROSION SCIENCE, 2018, 137 : 184 - 193
  • [22] Strength effect in stress corrosion cracking of high-strength steel in aqueous solution
    Li, HL
    Gao, KW
    Qiao, LJ
    Wang, YB
    Chu, WY
    CORROSION, 2001, 57 (04) : 295 - 299
  • [23] Strength effect in stress corrosion cracking of high-strength steel in aqueous solution
    Li, HL
    Hui, WJ
    Wang, YB
    Dong, H
    Weng, YQ
    Chu, WY
    ACTA METALLURGICA SINICA, 2001, 37 (05) : 512 - 516
  • [24] Strength effect in stress corrosion cracking of high-strength steel in aqueous solution
    Li, H.
    Hui, W.
    Wang, Y.
    Dong, H.
    Weng, Y.
    Chu, W.
    Jinshu Xuebao/Acta Metallurgica Sinica, 2001, 37 (05): : 512 - 516
  • [25] Effect of high energy shot peening pressure on the stress corrosion cracking of the weld joint of 304 austenitic stainless steel
    Lu Zhiming
    Shi Laimin
    Zhu Shenjin
    Tang Zhidong
    Jiang Yazhou
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2015, 637 : 170 - 174
  • [26] The effect of FSW parameters on the macro/micro-galvanic corrosion of the dissimilar joint between AZ31 and AA5052
    Safari, Saeed
    Nouripour, MohammadHossain
    Ghorbani, Mohammad
    Safari, Hossein
    MATERIALS CHEMISTRY AND PHYSICS, 2023, 305
  • [27] Influence of cerium on the formation of micro-galvanic corrosion elements of AZ91
    Zander, Daniela
    Heilig, Meredith
    Hort, Norbert
    Klaus, Gerald
    Buehrig-Polaczek, Andreas
    Groebner, Joachim
    Schmid-Fetzer, Rainer
    LIGHT METALS TECHNOLOGY V, 2011, 690 : 381 - +
  • [28] Fatigue assessment of fillet weld in steel bridge towers considering corrosion effects
    Jiang, Chao
    Xiong, Wen
    Cai, C. S.
    Zhou, Linyun
    Zhu, Yichen
    ENGINEERING FAILURE ANALYSIS, 2023, 143
  • [29] Micro-galvanic corrosion of duplex stainless steel annealed at different temperatures evaluated by experiments and a numerical simulation model
    Cao, Xinfeng
    Hu, Xiaojun
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2022, 73 (12): : 2019 - 2031
  • [30] Numerical study on the micro-galvanic corrosion of AZ31 magnesium alloy
    Gao, Fu-Yong
    Zhao, Ming
    He, Guang-Ping
    Fang, Ke-Ming
    Beijing Keji Daxue Xuebao/Journal of University of Science and Technology Beijing, 2013, 35 (05): : 634 - 641
12345