Effect of micro-galvanic corrosion on corrosion fatigue cracking of the weld joint of high strength bridge steel

被引：9
|
作者：
Li, Qi [1 ]
Yao, Qiong [2 ]
Sun, Liyang [1 ]
Ma, Hongchi [1 ]
Zhang, Chuang [2 ]
Wang, Ning [2 ]
机构：
[1] Univ Sci & Technol, Inst Adv Mat & Technol, Natl Mat Corros & Protect Data Ctr, Key Lab Corros & Protect MOE, Beijing 100083, Peoples R China
[2] Xichang Satellite Launch Ctr, Xichang 615000, Sichuan, Peoples R China
来源：
INTERNATIONAL JOURNAL OF FATIGUE | 2023年 / 170卷
基金：
中国国家自然科学基金;
关键词：
High-strength bridge steel; Marine atmosphere; Local electrochemical technique; Micro-galvanic corrosion; Corrosion fatigue failure; SCANNING KELVIN PROBE; E690; STEEL; FORCE MICROSCOPY; GROWTH-BEHAVIOR; CR; MICROSTRUCTURE;
D O I：
10.1016/j.ijfatigue.2023.107568
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
The local electrochemical and corrosion fatigue cracking behavior of the weld joint of Q690qE high-strength bridge steel was investigated in simulated marine environment. It reveals the weld joint was vulnerable to corrosion fatigue failure in polluted marine atmosphere with the corrosion fatigue life considerably lower than that of parent metal. The micro-galvanic corrosion effect between CGHAZ and WM played a dominant role in the corrosion fatigue failure of the weld joint, leading to the final fracture mostly at CGHAZ. The micro-galvanic corrosion was caused by Volta potential variation among various subzones, which was evidenced by local electrochemical techniques.
引用
收藏
页数：15
相关论文
共 50 条
  • [1] Numerical modeling of micro-galvanic corrosion
    Deshpande, Kiran B.
    ELECTROCHIMICA ACTA, 2011, 56 (04) : 1737 - 1745
  • [2] Corrosion fatigue cracking behaviors of Q690qE high-strength bridge steel as a weld joint in simulated marine environment
    Lu, Cuiping
    Yao, Qiong
    Li, Ningning
    Sun, Liyang
    Dai, Wenhe
    Zhang, Chuang
    Ma, Hongchi
    FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES, 2024, : 4341 - 4355
  • [3] Correlation of micro-galvanic corrosion behavior with corrosion rate in the initial corrosion process of dual phase steel
    Chen, Heng
    Lv, Zhaochong
    Lu, Lin
    Huang, Yunhua
    Li, Xiaogang
    JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2021, 15 : 3310 - 3320
  • [4] Fatigue Performance of Weld Joint for Railway Steel with High Corrosion
    Wang, Wen-Jing
    Tang, Wei
    Li, Si-Chun
    Li, Qiang
    INTERNATIONAL CONFERENCE ON MECHANICS AND MATERIALS ENGINEERING (ICMME 2014), 2014, : 477 - 482
  • [5] Micro-galvanic corrosion during formation of epoxy coating
    Feng, Zhenliang
    Song, Guang-Ling
    Xu, Yuqing
    Zheng, Dajiang
    Chen, Xiaodong
    PROGRESS IN ORGANIC COATINGS, 2020, 147
  • [6] Numerical Simulation of Micro-Galvanic Corrosion in Al Alloys: Steric Hindrance Effect of Corrosion Product
    Wang, Yongchao
    Yin, Litao
    Jin, Ying
    Pan, Jinshan
    Leygraf, Christofer
    JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 2017, 164 (14) : C1035 - C1043
  • [7] Gradient textures induce micro-galvanic corrosion on Mg
    Bai, Jing
    Sun, Chao
    Wang, Cheng
    Shao, Yi
    Meng, Jiao
    Dong, Qiangsheng
    Xue, Feng
    Chu, Chenglin
    JOURNAL OF ALLOYS AND COMPOUNDS, 2024, 1005
  • [8] An investigation of micro-galvanic corrosion in Al/AlNP composites
    Liu, ZhangSheng
    Wu, BianTao
    Gu, MingYuan
    MATERIALS CHEMISTRY AND PHYSICS, 2007, 102 (01) : 43 - 46
  • [9] Stress corrosion cracking behavior of welding joint of high strength steel
    Sepe, R.
    Bollino, F.
    Caiazzo, F.
    Berto, F.
    49TH ITALIAN ASSOCIATION FOR STRESS ANALYSIS CONFERENCE (AIAS 2020), 2021, 1038
  • [10] Numerical Simulation of Micro-Galvanic Corrosion in Al Alloys: Effect of Geometric Factors
    Yin, Litao
    Jin, Ying
    Leygraf, Christofer
    Birbilis, Nick
    Pan, Jinshan
    JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 2017, 164 (02) : C75 - C84
12345