Ultra-flexible Al2O3 fibers: A novel catalyst support material for sustainable catalysis

Flexible aluminum oxide (Al2O3) fibers were prepared by the blow spinning method and their potential as a high temperature catalyst support was investigated. The synthesized Al2O3 fibers exhibited remarkable flexibility in both mechanical compression and recovery tests, which remained intact in a wide temperature range from-196 degrees C to 1200 degrees C. Moreover, their low thermal conductivity of 0.030 W K1 center dot m- 1,demonstrated an outstanding thermal insulation. Subsequently, nickel nanoparticles were uniformly distributed on the surface of the Al2O3 fibers as a self-supporting catalyst using a conventional impregnation method. The resulting selfsupporting Ni/Al2O3 catalyst demonstrated remarkable thermo-catalytic performance and re-activation capability at high temperatures for thermocatalytic reaction of dry reforming of methane (DRM). Our findings highlight the potential of pure Al2O3 flexible fibers as a versatile material for various industrial applications, including high-temperature catalysis.