FATIGUE STRENGTH OF Al-Cu CAST ALLOY WITH DIFFERENT POURING TEMPERATURE

被引：0
|
作者：
Akhyar [1 ]
Iswanto, P. T. [2 ]
Malau, V. [2 ]
Putra, F. P. [2 ]
Farhan, A. [3 ]
机构：
[1] Univ Syiah Kuala, Dept Mech Engn, Jln Syech Abdurrauf 7, Banda Aceh 23111, Indonesia
[2] Gadjah Mada Univ UGM, Dept Mech & Ind Engn, Jln Grafika 2, Yogyakarta 55281, Indonesia
[3] FKIP Univ Syiah Kuala, Dept Phys Educ, Banda Aceh, Indonesia
来源：
METALURGIJA | 2024年 / 63卷 / 02期
关键词：
Al-Cu cast alloy; fatigue strength; tensile strength; pouring temperature; microstructure;
D O I：
暂无
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
This experiment aimed to evaluate how pouring temperature affects fatigue strength of Al-Cu cast alloy. Subsequently, commercial aluminum ingots, such as Al-2024 were remelted and then machined into samples for both tensile and fatigue testing. These samples were cast at three different temperature of 688, 738, and 788 oC while maintaining a constant mold temperature of 220 oC. The results showed that the highest tensile strength was 201,06 MPa at 738 oC. Additionally, the greatest fatigue strength was observed at 80,4 MPa at pouring temperature of 738 oC. It was observed that variations in pouring temperature can significantly impact fatigue strength of cast alloy. At the highest pouring temperature of 788 degrees C, the presence of pores in the metal casting samples resulted in a decrease in both tensile and fatigue strength. Furthermore, when examining the surface fractography of casting sample, the presence of brittle cracks in alloy was observed.
引用
收藏
页码：197 / 200
页数：4
相关论文
共 50 条
  • [41] Shot-Peening Effect on High Cycling Fatigue of Al-Cu Alloy
    Yasser Fouad
    Mostafa El Metwally
    Metallurgical and Materials Transactions A, 2013, 44 : 5488 - 5492
  • [42] The fatigue damage development in a cast Al-Si-Cu alloy
    Dietrich, Lech
    Radziejewska, Joanna
    MATERIALS & DESIGN, 2011, 32 (01) : 322 - 329
  • [43] Influence of alloy elements and pouring temperature on the fluidity of cast magnesium alloy
    Hua, Qin
    Gao, Deming
    Zhang, Hongjun
    Zhang, Yuhui
    Zhai, Qijie
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2007, 444 (1-2): : 69 - 74
  • [44] MEASUREMENTS OF SUPERPLASTICITY IN AN AL-CU ALLOY
    RAI, G
    GRANT, NJ
    METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1975, 6 (02): : 385 - 390
  • [45] Effect of aging treatment on microstructure and mechanical properties of centrifugally cast Al-Cu alloy
    Liu, Ai-Hui
    Sui, Yan-Wei
    Zhou, Guang-Hong
    Ding, Hong-Yan
    Zhang, Yue
    Cailiao Rechuli Xuebao/Transactions of Materials and Heat Treatment, 2011, 32 (12): : 94 - 97
  • [46] Effects of la on the age hardening behavior and precipitation kinetics in the cast Al-Cu alloy
    Jiang, Q. (jqc@jlu.edu.cn), 1600, Elsevier Ltd (540):
  • [47] Effects of La on the age hardening behavior and precipitation kinetics in the cast Al-Cu alloy
    Yao, Dongming
    Bai, Zhihao
    Qiu, Feng
    Li, Yanjun
    Jiang, Qichuan
    JOURNAL OF ALLOYS AND COMPOUNDS, 2012, 540 : 154 - 158
  • [48] Age Hardening and Mechanical Properties of Cast Al-Cu Alloy Modified by La and Pr
    Bai, Zhihao
    Qiu, Feng
    Liu, Yingying
    Zhou, Wei
    Jiang, Qichuan
    ADVANCED ENGINEERING MATERIALS, 2015, 17 (02) : 143 - 147
  • [49] SUPERPLASTICITY IN AL-CU EUTECTIC ALLOY
    HOLT, DL
    BACKOFEN, WA
    ASM TRANSACTIONS QUARTERLY, 1966, 59 (04): : 755 - &
  • [50] Welding of Al-Cu series alloy
    Okita, Tomiharu
    Keikinzoku Yosetsu/Journal of Light Metal Welding and Construction, 1995, 33 (04):
12345