FATIGUE STRENGTH OF Al-Cu CAST ALLOY WITH DIFFERENT POURING TEMPERATURE

被引：0
|
作者：
Akhyar [1 ]
Iswanto, P. T. [2 ]
Malau, V. [2 ]
Putra, F. P. [2 ]
Farhan, A. [3 ]
机构：
[1] Univ Syiah Kuala, Dept Mech Engn, Jln Syech Abdurrauf 7, Banda Aceh 23111, Indonesia
[2] Gadjah Mada Univ UGM, Dept Mech & Ind Engn, Jln Grafika 2, Yogyakarta 55281, Indonesia
[3] FKIP Univ Syiah Kuala, Dept Phys Educ, Banda Aceh, Indonesia
来源：
METALURGIJA | 2024年 / 63卷 / 02期
关键词：
Al-Cu cast alloy; fatigue strength; tensile strength; pouring temperature; microstructure;
D O I：
暂无
中图分类号：
TF [冶金工业];
学科分类号：
0806 ;
摘要：
This experiment aimed to evaluate how pouring temperature affects fatigue strength of Al-Cu cast alloy. Subsequently, commercial aluminum ingots, such as Al-2024 were remelted and then machined into samples for both tensile and fatigue testing. These samples were cast at three different temperature of 688, 738, and 788 oC while maintaining a constant mold temperature of 220 oC. The results showed that the highest tensile strength was 201,06 MPa at 738 oC. Additionally, the greatest fatigue strength was observed at 80,4 MPa at pouring temperature of 738 oC. It was observed that variations in pouring temperature can significantly impact fatigue strength of cast alloy. At the highest pouring temperature of 788 degrees C, the presence of pores in the metal casting samples resulted in a decrease in both tensile and fatigue strength. Furthermore, when examining the surface fractography of casting sample, the presence of brittle cracks in alloy was observed.
引用
收藏
页码：197 / 200
页数：4
相关论文
共 50 条
  • [1] Effects of Mold Temperature and Pouring Temperature on the Hot Tearing of Cast Al-Cu Alloys
    Shimin Li
    Kumar Sadayappan
    Diran Apelian
    Metallurgical and Materials Transactions B, 2016, 47 : 2979 - 2990
  • [2] Effects of Mold Temperature and Pouring Temperature on the Hot Tearing of Cast Al-Cu Alloys
    Li, Shimin
    Sadayappan, Kumar
    Apelian, Diran
    METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 2016, 47 (05): : 2979 - 2990
  • [3] Nanoparticle additions promote outstanding fracture toughness and fatigue strength in a cast Al-Cu alloy
    Yang, Chenglin
    Zhao, Qinglong
    Zhang, Zhenjun
    Li, Linlin
    Tian, Weisi
    Liu, Rui
    Zhang, Peng
    Xu, Yijiang
    Li, Yanjun
    Zhang, Zhefeng
    Jiang, Qichuan
    Ritchie, Robert O.
    MATERIALS & DESIGN, 2020, 186
  • [4] Effects of different pouring conditions on the micro-structure of Al-Cu alloy
    Shandong Institute of Architecture and Engineering, Ji'nan 250101, China
    不详
    Tezhong Zhuzao Ji Youse Hejin, 2006, 1 (10-12):
  • [5] Characterization of an Al-Cu cast alloy
    Talamantes-Silva, M. A.
    Rodriguez, A.
    Talamantes-Silva, J.
    Valtierra, S.
    Colas, Rafael
    MATERIALS CHARACTERIZATION, 2008, 59 (10) : 1434 - 1439
  • [6] ANOMALOUS EFFECT OF TEMPERATURE AND STRAIN RATE ON THE STRENGTH OF AS-CAST AL-CU EUTECTIC ALLOY
    KALE, SS
    KASHYAP, BP
    SCRIPTA METALLURGICA ET MATERIALIA, 1992, 26 (06): : 975 - 979
  • [7] Evolution of microstructure in centrifugal cast Al-Cu alloy
    Sui Yanwei1
    2.School of Materials Science and Engineering
    3.Department of Mechanical Engineering
    ChinaFoundry, 2010, 7 (01) : 43 - 46
  • [8] Evolution of microstructure in centrifugal cast Al-Cu alloy
    Sui Yanwei
    Li Bangsheng
    Liu Aihui
    Guo Jingjie
    Fu Hengzhi
    CHINA FOUNDRY, 2010, 7 (01) : 43 - 46
  • [9] Fatigue behavior of Al-Cu alloy subjected to different numbers of ECAP passes
    Fang, Daran
    Zhang, Peng
    Duan, Qiqiang
    Wu, Shiding
    Zhang, Zhefeng
    Li, Jiajun
    Zhao, Naiqin
    ADVANCED ENGINEERING MATERIALS, 2007, 9 (10) : 860 - 866
  • [10] OPTIMIZATION OF HIGH-TEMPERATURE COMPRESSION OF AS-CAST AL-CU EUTECTIC ALLOY
    NASSEF, GA
    ELASHRAM, A
    SUERY, M
    METALS TECHNOLOGY, 1984, 11 (MAY): : 196 - 200
12345