Copper plating on bonding properties of aluminium/steel explosive welded composite plate

被引：4
|
作者：
Bi, Zhixiong [1 ,2 ]
Li, Xuejiao [2 ,3 ]
Yang, Ke [3 ]
Wang, Quan [2 ]
Kai, Rong [3 ]
Dai, Xiande [2 ]
机构：
[1] Anhui Univ Sci & Technol, Sch Civil Engn, Huainan, Peoples R China
[2] Anhui Univ Sci & Technol, Sch Chem Engn, Huainan, Peoples R China
[3] Anhui Univ Sci & Technol, Sch Min Engn, Huainan, Peoples R China
来源：
MATERIALS SCIENCE AND TECHNOLOGY | 2023年 / 39卷 / 03期
基金：
中国国家自然科学基金;
关键词：
Explosive welding; copper plating; microscopic morphology; weldability window; numerical simulation; MECHANICAL-PROPERTIES; MICROSTRUCTURE; INTERFACE; STEEL; MODEL;
D O I：
10.1080/02670836.2022.2116874
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
In order to reduce critical impact velocity and enlarge weldability window of aluminium/steel explosive welding, a chemical copper plating layer as interlayer was proposed to carry out aluminium/steel explosive welding. The results showed that the interface of the 1060/Q235 composite plate had good bonding performance, and no obvious defects such as cracks and pores were found. Copper plating as intermediate layer could enlarge aluminium/steel weldability window. The thickness of solidified melt was much thicker than that of diffusion zone. The molten copper particles participated in the formation of re-entry jet, which rotated under the action of initial jet. The presence of the Cu layer reduces the occurrence of excessive melting during welding and improves the properties of the interface.
引用
收藏
页码：392 / 402
页数：11
相关论文
共 50 条
  • [21] ELECTRICAL PROPERTIES OF TIG WELDED JOINTS BETWEEN COPPER AND ALUMINIUM
    VOROPAI, NM
    ARTAMONO.NM
    AUTOMATIC WELDING USSR, 1966, 19 (10): : 63 - &
  • [22] Interfacial bonding properties of titanium foil/steel explosive welding
    Bi Z.
    Li X.
    Wu Y.
    Xiong S.
    Wang Q.
    Rong K.
    Hanjie Xuebao/Transactions of the China Welding Institution, 2022, 43 (04): : 81 - 85
  • [23] Microstructural features of joint zones in an explosive welded Al/Ti/steel plate system
    Wuhan Transportation University, Wuhan 430063, China
    不详
    Jinshu Xuebao/Acta Metallurgica Sinica, 1997, 33 (11): : 1205 - 1206
  • [24] INFLUENCE OF ALLOYING ELEMENTS IN STEEL ON PROPERTIES OF STEEL-ALUMINIUM WELDED JOINTS
    RYABOV, VR
    WELDING PRODUCTION, 1971, 18 (04): : 13 - &
  • [25] Parameters of the interfacial waves of Zr/steel composite plate by explosive welding
    Wang, Xiaoxu
    Wang, Jinxiang
    Zhao, Zheng
    He, Yong
    Wang, J. (wjx@njust.edu.cn), 1600, Science Press (43): : 682 - 685
  • [26] Parameters of the Interfacial Waves of Zr/Steel Composite Plate by Explosive Welding
    Wang Xiaoxu
    Wang Jinxiang
    Zhao Zheng
    He Yong
    RARE METAL MATERIALS AND ENGINEERING, 2014, 43 (03) : 682 - 685
  • [27] Effect of corrosion on the surface properties of steel plate and interfacial bonding properties between CFRP plate and corroded steel plate
    Li A.
    Xu S.
    Fuhe Cailiao Xuebao/Acta Materiae Compositae Sinica, 2022, 39 (02): : 746 - 758
  • [28] Influence of normalizing on microstructure and mechanical properties of Cu/Al explosive welded plate
    Zhou G.
    Ma H.
    Shen Z.
    Yang M.
    Chen P.
    Hanjie Xuebao/Transactions of the China Welding Institution, 2019, 40 (06): : 46 - 51
  • [29] Effects of annealing and hot-rolling on properties and microstructure of explosion-welded composite steel plate
    Liao, Dongbo
    Zha, Wusheng
    Li, Wei
    Zha, W. (zhawusheng684@hotmail.com), 2013, Harbin Research Institute of Welding (34): : 109 - 112
  • [30] An investigation of the shearing performance and sheared surface characterisation of ultra-strength DP steel-Al explosive welded plate composite
    Demir, Bilge
    Ali, Khalil Belras
    Gurun, Hakan
    Acarer, Mustafa
    INTERNATIONAL JOURNAL OF ADVANCED MANUFACTURING TECHNOLOGY, 2023, 126 (5-6): : 1845 - 1861
12345