Post-mortem analysis of MgO-Al2O3-C bricks containing bauxite used in steel ladle walls

A serious problem with integrated masonry linings ladle was that the ladle wall bricks were difficult to be partially replaced. Thus, the service life of the ladle was determined by the properties of ladle wall bricks. In this study, the new generation of MgO-Al2O3-C bricks with bauxite aggregates was tested in a ladle lining of an integrated steel ladle for 103 cycles, and the corroded microstructure of the used brick was investigated. A multilayered structure of bauxite aggregates could be observed in the used brick, which inhibited the slag penetration along the boundary of the magnesia aggregates and reduced the degree of the aggregates fall off from the used bricks. Besides, during the process of slag penetration, bauxite aggregates could melt into the slag, which increased the viscosity of the slag and weakened the penetration ability of the slag. The MgO-Al2O3-C bricks with bauxite addition could improve the service life of the ladle to a certain extent.