The influence of quaternary ammonium salts on mechanical properties of light-cured resin dental composites

被引：3
|
作者：
Zalega, Maja [1 ]
Nowak, Joanna [2 ]
Bociong, Kinga [1 ]
机构：
[1] Med Univ Lodz, Dept Gen Dent, Ul Pomorska 251, PL-92213 Lodz, Poland
[2] Med Univ Lodz, Lab Mat Res, Ul Pomorska 251, PL-92213 Lodz, Poland
来源：
POLIMERY | 2023年 / 68卷 / 04期
关键词：
dental composites; quaternary ammonium salts; mechanical properties; POLYMERIZATION SHRINKAGE; STRESS; ADHESIVE; STRENGTH; HARDNESS;
D O I：
10.14314/polimery.2023.4.1
中图分类号：
O63 [高分子化学（高聚物）];
学科分类号：
070305 ; 080501 ; 081704 ;
摘要：
The composite consisting of bis-GMA/UDMA/HEMA/TEGDMA monomer mixture forming a polymer matrix filled with silanized silica (45 wt%) was modified with CTAB or DODAB quaternary ammonium salts (0.5-2.0 wt%). The hardness, flexural strength as well as diametrical tensile strength of the composite before and after modification were evaluated. The type and amount of salt affected the hardness, flexural strength, and shrinkage stress; however, they did not influence the diametral tensile strength of the tested composites.
引用
收藏
页码：195 / 205
页数：11
相关论文
共 50 条
  • [31] POSTERIOR LIGHT-CURED COMPOSITES
    COWAN, DJJ
    BRITISH DENTAL JOURNAL, 1984, 157 (07) : 226 - 226
  • [32] LIGHT-CURED RESIN FOR POST PATTERNS
    WALDMEIER, MD
    GRASSO, JE
    JOURNAL OF PROSTHETIC DENTISTRY, 1992, 68 (03): : 412 - 415
  • [33] Influence of paste temperature at curing on conversion rate and bending strength of light-cured dental composites
    Li, J
    Nicander, I
    vonBeetzen, M
    Sundstrom, F
    JOURNAL OF ORAL REHABILITATION, 1996, 23 (05) : 298 - 301
  • [34] RESIN COMPOSITION VARIATION AND MECHANICAL-PROPERTIES OF LIGHT CURED COMPOSITES
    WAKNINE, S
    VAIDYANATHAN, J
    VAIDYANATHAN, TK
    SCHULMAN, A
    JOURNAL OF DENTAL RESEARCH, 1984, 63 : 292 - 292
  • [35] Five-year color changes of light-cured resin composites: influence of light-curing times
    Hosoya, Y
    DENTAL MATERIALS, 1999, 15 (04) : 268 - 274
  • [36] Effect of hybrid reinforcements on the curing kinetics and mechanical properties of light-cured polymer composites
    Yao, Jiaqi
    Wang, Kun
    Wang, Zhengzhi
    POLYMER COMPOSITES, 2024, 45 (10) : 9588 - 9599
  • [37] Effect of immersion in water or thermal cycling on the mechanical properties of light-cured composites.
    Bae, TS
    Baek, SH
    Chu, YH
    Park, CW
    Kondo, S
    JOURNAL OF DENTAL RESEARCH, 1996, 75 (05) : 1260 - 1260
  • [38] Polymerisation shrinkage of light-cured hydroxyapatite (HA)-reinforced dental composites
    Oduncu, Bilge S.
    Yucel, Sevil
    Aydin, Ismail
    Sener, Isil D.
    Yamaner, Gokhan
    World Academy of Science, Engineering and Technology, 2010, 64 : 286 - 291
  • [39] CURE PROFILES OF LIGHT-CURED DENTAL COMPOSITES BY RAMAN-SPECTROSCOPY
    LOUDEN, JD
    ROBERTS, TA
    JOURNAL OF RAMAN SPECTROSCOPY, 1983, 14 (05) : 365 - 366
  • [40] Polymerisation shrinkage of light-cured hydroxyapatite (HA)-reinforced dental composites
    Oduncu, Bilge S.
    Yucel, Sevil
    Aydin, Ismail
    Sener, Isil D.
    Yamaner, Gokhan
    World Academy of Science, Engineering and Technology, 2010, 40 : 286 - 291
12345