Study on high-temperature oxidation and hot corrosion characteristics of Cr60Ni40 laser cladding layer

被引：6
|
作者：
Chen, Shanshan [1 ]
Liu, Zongde [1 ]
Ning, Huaqing [1 ]
Liu, Fulai [1 ]
机构：
[1] North China Elect Power Univ, Key Lab Energy Transfer & Syst Power Stn, Minist Educ, Beijing 102206, Peoples R China
来源：
MATERIALS LETTERS | 2023年 / 342卷
关键词：
Cr-based alloy; Laser cladding; Corrosion; Oxidation; Microstructure; ALLOY;
D O I：
10.1016/j.matlet.2023.134352
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
In order to investigate the high-temperature characteristics of Cr-based alloy, Cr60Ni40 laser cladding layer (60 wt% Cr and 40 wt% Ni) were prepared and subjected to high-temperature oxidation test and hot corrosion test. The results prove that there are Cr segregation and large particles of Cr precipitated within the raw Cr60Ni40 cladding layer. During the high-temperature test, Cr2O3 protective film was generated on the surface of the cladding layer, protecting the substrate to different degrees. However, the particles precipitation of Cr caused uneven growth of Cr-rich oxide, and the Cr segregation brought about internal corrosion with Cr2O3 as the main products.
引用
收藏
页数：3
相关论文
共 50 条
  • [21] Microstructure and Wear Resistance of Ni-Cr Alloy Laser Cladding Layer with High Cr Content
    Pan, Chaoyang
    Liu, Zongde
    Shen, Yue
    Lu, Xinjie
    Mao, Jie
    Wang, Xinyu
    Li, Jiaxuan
    RARE METAL MATERIALS AND ENGINEERING, 2024, 53 (09) : 2438 - 2445
  • [22] IMPROVING HIGH-TEMPERATURE OXIDATION OF INCOLOY-800H BY LASER CLADDING
    DEDAMBORENEA, J
    LOPEZ, V
    VAZQUEZ, AJ
    SURFACE & COATINGS TECHNOLOGY, 1994, 70 (01): : 107 - 113
  • [23] High-Temperature Oxidation and Smelt Deposit Corrosion of Ni-Cr-Ti Arc-Sprayed Coatings
    S. Matthews
    M. Schweizer
    Journal of Thermal Spray Technology, 2013, 22 : 932 - 946
  • [24] High-Temperature Oxidation and Smelt Deposit Corrosion of Ni-Cr-Ti Arc-Sprayed Coatings
    Matthews, S.
    Schweizer, M.
    JOURNAL OF THERMAL SPRAY TECHNOLOGY, 2013, 22 (06) : 932 - 946
  • [25] High-temperature oxidation and hydrothermal corrosion of textured Cr2AlC-based coatings on zirconium alloy fuel cladding
    Tang, Chongchong
    Grosse, Mirco
    Ulrich, Sven
    Klimenkov, Michael
    Jaentsch, Ute
    Seifert, Hans Juergen
    Stueber, Michael
    Steinbrueck, Martin
    SURFACE & COATINGS TECHNOLOGY, 2021, 419
  • [26] Effect of Power on Microstructure and Hot Corrosion of Induction-Assisted Ultra-High-Speed Ni60 Laser Cladding
    Liu, Ao
    Chen, Lan
    Zhang, Xinzhou
    Zhu, Lei
    Li, Yunze
    Yu, Tianqi
    Ren, Xudong
    JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2025,
  • [27] STUDY OF NI77-CR21-SI-AL ALLOY OXIDATION AT HIGH-TEMPERATURE
    CHEN, XS
    ARMANET, F
    BERANGER, G
    MEMOIRES ET ETUDES SCIENTIFIQUES DE LA REVUE DE METALLURGIE, 1991, 88 (10): : 703 - 710
  • [28] Effect of Cr Content on Corrosion Resistance of Ni-xCr-Mo Laser-Cladding Coatings under H2S-Induced High-Temperature Corrosion Atmosphere
    Liu, Congcong
    Liu, Zongde
    Gao, Yuan
    Wang, Xinyu
    Zheng, Chao
    MATERIALS, 2022, 15 (05)
  • [29] Study on High-Temperature Oxidation Behavior of Electrodeposited Ni/Cr Coating on Zr Alloy Surface
    Zhu, Li'an
    Yuan, Weichao
    Wang, Shuxiang
    Wang, Zhen
    Ye, Yicong
    Bai, Shuxin
    RARE METAL MATERIALS AND ENGINEERING, 2024, 53 (10) : 2805 - 2822
  • [30] Evolution of oxide layer during high-temperature oxidation of NiCoCrAlY coating via laser cladding on 304 stainless steel
    Nie, Jinhao
    Li, Yuxin
    Chen, Bowen
    Yang, Yixin
    Zhang, Hongjian
    Liu, Siyuan
    Wei, Shouzheng
    Cai, Jie
    Guan, Qingfeng
    MATERIALS LETTERS, 2021, 286
12345