Study on high-temperature oxidation and hot corrosion characteristics of Cr60Ni40 laser cladding layer

被引：6
|
作者：
Chen, Shanshan [1 ]
Liu, Zongde [1 ]
Ning, Huaqing [1 ]
Liu, Fulai [1 ]
机构：
[1] North China Elect Power Univ, Key Lab Energy Transfer & Syst Power Stn, Minist Educ, Beijing 102206, Peoples R China
来源：
MATERIALS LETTERS | 2023年 / 342卷
关键词：
Cr-based alloy; Laser cladding; Corrosion; Oxidation; Microstructure; ALLOY;
D O I：
10.1016/j.matlet.2023.134352
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
In order to investigate the high-temperature characteristics of Cr-based alloy, Cr60Ni40 laser cladding layer (60 wt% Cr and 40 wt% Ni) were prepared and subjected to high-temperature oxidation test and hot corrosion test. The results prove that there are Cr segregation and large particles of Cr precipitated within the raw Cr60Ni40 cladding layer. During the high-temperature test, Cr2O3 protective film was generated on the surface of the cladding layer, protecting the substrate to different degrees. However, the particles precipitation of Cr caused uneven growth of Cr-rich oxide, and the Cr segregation brought about internal corrosion with Cr2O3 as the main products.
引用
收藏
页数：3
相关论文
共 50 条
  • [1] High-Temperature Oxidation and Hot Corrosion Characteristics of Ni-Cr Alloy Cladding Layers with Different Cr Contents
    Chen, Shanshan
    Liu, Zongde
    Pan, Chaoyang
    Liu, Fulai
    Fu, Yundi
    Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering, 2023, 52 (08): : 2702 - 2710
  • [2] High-Temperature Oxidation and Hot Corrosion Characteristics of Ni-Cr Alloy Cladding Layers with Different Cr Contents
    Chen Shanshan
    Liu Zongde
    Pan Chaoyang
    Liu Fulai
    Fu Yundi
    RARE METAL MATERIALS AND ENGINEERING, 2023, 52 (08) : 2702 - 2710
  • [3] Chlorine-induced high-temperature corrosion characteristics of Ni-Cr alloy cladding layer and Ni-Cr-Mo alloy cladding layer
    Wang, Xinyu
    Liu, Zongde
    Cheng, Kehan
    Kong, Yao
    CORROSION SCIENCE, 2023, 216
  • [4] Laser cladding Ni35Al2OFe intermetallic coating for resisting high-temperature oxidation and hot corrosion
    Xu, XY
    Zhong, ML
    Liu, WJ
    LASERS IN MATERIAL PROCESSING AND MANUFACTURING, 2002, 4915 : 227 - 233
  • [5] Effect of Si on High-Temperature Corrosion Resistance of Ni-Cr-Mo Alloy Cladding Layer
    Chen Shanshan
    Liu Zongde
    Pan Chaoyang
    Cheng Kehan
    Shen Yue
    RARE METAL MATERIALS AND ENGINEERING, 2023, 52 (07) : 2343 - 2352
  • [6] Effect of Si on High-Temperature Corrosion Resistance of Ni-Cr-Mo Alloy Cladding Layer
    Chen, Shanshan
    Liu, Zongde
    Pan, Chaoyang
    Cheng, Kehan
    Shen, Yue
    Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering, 2023, 52 (07): : 2343 - 2352
  • [7] High-temperature oxidation and hot corrosion of Cr2AlC
    Lin, Z. J.
    Li, M. S.
    Wang, J. Y.
    Zhou, Y. C.
    ACTA MATERIALIA, 2007, 55 (18) : 6182 - 6191
  • [8] LASER CLADDING OF NI-CR-AL-HF ON INCONEL 718 FOR IMPROVED HIGH-TEMPERATURE OXIDATION RESISTANCE
    SINGH, J
    NAGARATHNAM, K
    MAZUMDER, J
    HIGH TEMPERATURE TECHNOLOGY, 1987, 5 (03): : 131 - 137
  • [9] HIGH-TEMPERATURE OXIDATION AND HOT CORROSION BEHAVIOR OF SOME INORGANIC COATED 18 CR-8.5 NI STEEL
    MALIK, AU
    AHMED, S
    INDIAN JOURNAL OF TECHNOLOGY, 1979, 17 (04): : 156 - 157
  • [10] CHLORIDE EFFECTS IN HIGH-TEMPERATURE OXIDATION AND HOT CORROSION
    SHORES, DA
    MCKEE, DW
    SPACIL, HS
    JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1976, 123 (08) : C252 - C252
12345