Anisotropic thermomechanical fatigue of a nickel-base single-crystal superalloy Part I: Effects of crystal orientations and damage mechanisms

被引：22
|
作者：
Luo, Cheng [1 ]
Yuan, Huang [1 ,2 ]
机构：
[1] Tsinghua Univ, Sch Aerosp Engn, Beijing, Peoples R China
[2] Tsinghua Univ, Inst Aero Engines, Beijing, Peoples R China
来源：
INTERNATIONAL JOURNAL OF FATIGUE | 2023年 / 168卷
关键词：
Thermomechanical fatigue; Damage mechanism; Fatigue-creep-oxidation; Crystal orientation; LOW-CYCLE FATIGUE; CRACK INITIATION; BEHAVIOR; TEMPERATURE; DEFORMATION; OXIDATION; CREEP;
D O I：
10.1016/j.ijfatigue.2022.107438
中图分类号：
TH [机械、仪表工业];
学科分类号：
0802 ;
摘要：
Thermomechanical fatigue in distinct crystal orientations of nickel-base single-crystal superalloy was studied. Crack initiation modes and damage mechanisms were characterized on fracture surfaces and longitudinal sections by scanning electron microscope and optical microscope. Creep damage nucleated from casting pores in IP-TMF and propagated under mode I. The creep facets were controlled by the activated slip systems, whereas fatigue damage was orientation-dependent and developed by slipping along different crystallographic planes. Oxidation-assisted cracking in OP-TMF tests was non-crystallographic for all crystal orientations. Multi -layer structures near the crack tip revealed successive growth of oxide and the crack grew within the oxidized material.
引用
收藏
页数：16
相关论文
共 50 条
  • [21] THE EFFECT OF INTERNAL HYDROGEN ON A SINGLE-CRYSTAL NICKEL-BASE SUPERALLOY
    WALSTON, WS
    BERNSTEIN, IM
    THOMPSON, AW
    METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1992, 23 (04): : 1313 - 1322
  • [22] HYDROGEN EFFECTS IN CMSX-2, A NICKEL-BASE SUPERALLOY SINGLE-CRYSTAL
    BAKER, CL
    CHENE, J
    BERNSTEIN, IM
    WILLIAMS, JC
    JOURNAL OF METALS, 1985, 37 (08): : A72 - A72
  • [23] Thermomechanical fatigue crack growth in a single crystal nickel base superalloy
    Palmert, Frans
    Moverare, Johan
    Gustafsson, David
    INTERNATIONAL JOURNAL OF FATIGUE, 2019, 122 : 184 - 198
  • [24] Anisotropic Stress Rupture Behavior of a Nickel-Base Single Crystal Superalloy
    Han Guoming
    Yu Jinjiang
    Sun Xiaofeng
    Guan Hengrong
    Hu Zhuangqi
    RARE METAL MATERIALS AND ENGINEERING, 2011, 40 (04) : 673 - 676
  • [25] OBSERVATIONS AND CHARACTERIZATION CONSIDERATIONS OF FATIGUE CRACK-GROWTH IN A SINGLE-CRYSTAL NICKEL-BASE SUPERALLOY
    WU, DC
    HOEPPNER, DW
    SCRIPTA METALLURGICA, 1985, 19 (04): : 493 - 498
  • [26] THE INFLUENCE OF MICROSTRUCTURE ON HYDROGEN ENVIRONMENT EMBRITTLEMENT AND FATIGUE RESPONSE OF A SINGLE-CRYSTAL NICKEL-BASE SUPERALLOY
    FRITZEMEIER, LG
    JOURNAL OF METALS, 1985, 37 (11): : A11 - A11
  • [27] Stray grain formation in nickel-base superalloy single-crystal welds
    Vitek, JM
    Babu, SS
    Park, JW
    David, SA
    SOLIDIFICATION PROCESSES AND MICROSTRUCTURES: A SYMPOSIUM IN HONOR OF WILFRIED KURZ, 2004, : 61 - 66
  • [28] HYDROGEN EFFECTS ON LOW-CYCLE FATIGUE OF THE SINGLE-CRYSTAL NICKEL-BASE SUPERALLOY CMSX-2
    DOLLAR, M
    BERNSTEIN, IM
    DOMNANOVITCH, A
    KROMP, W
    PINCZOLITS, H
    METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1991, 22 (11): : 2597 - 2603
  • [29] MICROSTRUCTURAL EVOLUTION OF AN OVERLAY COATING ON A SINGLE-CRYSTAL NICKEL-BASE SUPERALLOY
    TOTEMEIER, TC
    GALE, WF
    KING, JE
    METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1994, 25 (12): : 2837 - 2840
  • [30] VIBRATION OF NICKEL-BASE SINGLE-CRYSTAL AND DIRECTIONALLY SOLIDIFIED SUPERALLOY PLATES
    HASEBE, T
    SAKANE, M
    OHNAMI, M
    JSME INTERNATIONAL JOURNAL SERIES A-MECHANICS AND MATERIAL ENGINEERING, 1994, 37 (04): : 481 - 487
12345