Oxidation behavior of CrAl coating with and without Nb addition in high temperature steam environment

被引：2
|
作者：
Zeng, Song [1 ]
Li, Junfeng [2 ]
Chen, Chen [1 ]
Meng, Yan [1 ]
Zhu, Chaowen [1 ]
Bao, Yiwang [2 ]
Han, Xiaochun [1 ]
Zhang, Haibin [1 ]
机构：
[1] China Acad Engn Phys, Inst Nucl Phys & Chem, Innovat Res Team Adv Ceram, Mianyang 621900, Peoples R China
[2] China Bldg Mat Acad, State Key Lab Green Bldg Mat, Beijing 100024, Peoples R China
来源：
JOURNAL OF NUCLEAR MATERIALS | 2023年 / 581卷
基金：
中国国家自然科学基金;
关键词：
CrAl coating; Nb addition; Al; 2; O; 3; oxide; High temperature oxidation; DEGREES-C; FE ALLOYS; AL; RESISTANCE; ZIRCALOY-4; DIFFUSION; KINETICS; DEPOSITION; STABILITY; TI2ALC;
D O I：
10.1016/j.jnucmat.2023.154437
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
CrAl coatings with and without Nb addition are fabricated and their oxidation behavior at 10 0 0 & DEG;C and 1100 & DEG;C is investigated. Results reveal that Nb addition has a positive effect on forming the stable Al2O3 layer. The oxide layer changes from a porous Al2O3 layer with internal Al2O3 oxides in the CrAl coating into a single dense Al2O3 layer in the CrAl-1.5Nb coating. Adding Nb can significantly maintain the Al inventory of the CrAl coating as well as suppress the outward diffusion of Zr by grain boundary pinning effect, and increases the activity of Al to form a stable Al2O3 layer on the surface, which improve the oxidation performance of CrAl coatings.& COPY; 2023 Elsevier B.V. All rights reserved.
引用
收藏
页数：14
相关论文
共 50 条
  • [41] High temperature oxidation behavior of arc-sprayed FeCrBAlMo coating
    Wang, Zehua (zhwang@hhu.edu.cn), 1600, J.AOTs Sycamore Global Publications LLC (19):
  • [42] High Temperature Oxidation Behavior of Arc-sprayed FeCrBAlMo Coating
    Zhang, Xin
    Wang, Zehua
    Zhou, Zehua
    Lin, Jinran
    JOURNAL OF ADVANCED OXIDATION TECHNOLOGIES, 2016, 19 (01) : 105 - 112
  • [43] HIGH TEMPERATURE OXIDATION BEHAVIOR OF A (MCrAlY plus AlSiY) COMPOSITE COATING
    Peng Xin
    Jiang Sumeng
    Duan Xuhai
    Gong Jun
    Sun Chao
    ACTA METALLURGICA SINICA, 2009, 45 (03) : 378 - 384
  • [44] Oxidation Behavior of Pd-modified aluminide coating at high temperature
    Li, MJ
    Sun, XF
    Guan, HR
    Jiang, XX
    Hu, ZQ
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2003, 19 (03) : 213 - 217
  • [45] Oxidation behavior of a nanocrystalline coating with low Ta content at high temperature
    Yang, Lanlan
    Wang, Jinlong
    Yang, Ruize
    Yang, Shasha
    Jia, Yixuan
    Chen, Minghui
    Qiao, Yanxin
    Guo, Pingyi
    Zhu, Shenglong
    Wang, Fuhui
    CORROSION SCIENCE, 2021, 180
  • [46] High-temperature oxidation behavior of sputtered IN 738 nanocrystalline coating
    Geng, SJ
    Wang, FH
    Zhu, SL
    OXIDATION OF METALS, 2002, 57 (3-4): : 231 - 243
  • [47] High temperature oxidation behavior of SiC coating in TRISO coated particles
    Liu, Rongzheng
    Liu, Bing
    Zhang, Kaihong
    Liu, Malin
    Shao, Youlin
    Tang, Chunhe
    JOURNAL OF NUCLEAR MATERIALS, 2014, 453 (1-3) : 107 - 114
  • [48] High temperature oxidation behavior of NiCrAlY coating by arc ion plating
    Wang, B.
    Wang, A.-Y.
    Sun, C.
    Huang, R.-F.
    Wen, L.-S.
    Chinese Journal of Aeronautics, 2001, 14 (02) : 106 - 111
  • [49] High temperature oxidation behavior of TiAl alloy with electrodeposited SiOC coating
    Yan, Hao-Jie
    Li, Yun-Yang
    Yin, Ruo-Zhan
    Sun, Qing-Qing
    Liu, Hui-Jun
    Zeng, Chao-Liu
    Wu, Lian-Kui
    Cao, Fa-He
    CORROSION SCIENCE, 2023, 224
  • [50] High temperature oxidation behavior of Pd-Ni-Al coating
    Li, MJ
    Sun, XF
    Guan, HR
    Jiang, XX
    Hu, ZQ
    ACTA METALLURGICA SINICA, 2003, 39 (07) : 755 - 760
12345