Study on fatigue damage and fatigue crack propagation of rubber concrete

被引：26
|
作者：
Liu, Miaoyan [1 ]
Lu, Jun [1 ,2 ]
Jiang, Wenhao [1 ]
Ming, Pan [1 ]
机构：
[1] Nanjing Hydraul Res Inst, Nanjing 210029, Peoples R China
[2] State Key Lab Hydrol Water Resources & Hydraul Eng, Nanjing 210098, Peoples R China
来源：
JOURNAL OF BUILDING ENGINEERING | 2023年 / 65卷
关键词：
Rubber concrete; Fatigue; Crack extension; Hysteresis phenomenon; Acoustic emission; Damage;
D O I：
10.1016/j.jobe.2022.105718
中图分类号：
TU [建筑科学];
学科分类号：
0813 ;
摘要：
In order to study the crack propagation process and damage mechanism of rubber concrete under fatigue loading, the fatigue test of plain concrete beam and rubber concrete beam with precast cracks was carried out, and the loading process was monitored in real time by acoustic emission. The results show that after the addition of rubber, the maximum deformation of rubber concrete under fatigue load is about twice that of plain concrete, and the fatigue life and fracture energy increase. It is confirmed by AE signals that there is hysteresis between cracks and loads under fatigue load due to the lag of energy transfer. The incorporation of rubber particles also reduces the range of changes in stress strength factors. The b-value of AE reflects the damage state and crack development of the concrete. When the b-value is reduced to 0.8, it can be used as an early warning indicator of structural failure.
引用
收藏
页数：15
相关论文
共 50 条
  • [41] The study of the fatigue crack propagation in mixed mode crack growth
    Vshivkov, A.
    Iziumova, A.
    Plekhov, O.
    2ND INTERNATIONAL CONFERENCE ON STRUCTURAL INTEGRITY, ICSI 2017, 2017, 5 : 438 - 445
  • [42] Experimental study on fracture and fatigue crack propagation processes in concrete based on DIC technology
    Li, Dongyang
    Huang, Peiyan
    Chen, Zhanbiao
    Yao, Guowen
    Guo, Xinyan
    Zheng, Xiaohong
    Yang, Yi
    ENGINEERING FRACTURE MECHANICS, 2020, 235
  • [43] Fatigue crack propagation of rubber toughened epoxy adhesives under mode I loading (effects of rubber content and adhesive thickness on fatigue crack growth)
    Miyazaki, Katsumasa
    Fujii, Toru
    Nippon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A, 1995, 61 (586): : 1212 - 1217
  • [44] Surface fatigue crack propagation behavior in a residual stress field: (Fatigue crack growth law and evaluation of fatigue crack propagation rate)
    Torii, Tashiyuki
    Honda, Kazuo
    Sugiyama, Masahiko
    Nippon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A, 1988, 54 (505): : 1723 - 1730
  • [45] FATIGUE CRACK PROPAGATION - AN ANALYSIS
    TOMKINS, B
    PHILOSOPHICAL MAGAZINE, 1968, 18 (155) : 1041 - +
  • [46] HSST - FATIGUE AND CRACK PROPAGATION
    WITT, FJ
    NUCLEAR SAFETY, 1970, 11 (04): : 331 - +
  • [47] DAMAGE OF CONCRETE IN FATIGUE
    ALLICHE, A
    FRANCOIS, D
    JOURNAL OF ENGINEERING MECHANICS-ASCE, 1992, 118 (11): : 2176 - 2190
  • [48] Calculation of fatigue crack propagation
    B. G. Nesterenko
    Journal of Machinery Manufacture and Reliability, 2007, 36 (5) : 450 - 453
  • [49] On the entropy of fatigue crack propagation
    Hajshirmohammadi, B.
    Khonsari, M. M.
    INTERNATIONAL JOURNAL OF FATIGUE, 2020, 133
  • [50] FATIGUE CRACK PROPAGATION IN METALS
    FROST, NE
    DIXON, JR
    NATURE, 1966, 212 (5070) : 1569 - &
12345