Thermodynamic modeling of the Mg-Nd-Sr ternary system with key experimental investigation

The phase equilibria in the Mg-rich region of the Mg-Nd-Sr ternary system at 300 and 350 degrees C were established using equilibrated-sample method. Powder X-ray diffraction (XRD) technique and scanning electron microscopy (SEM) equipped with energy-dispersive spectroscopy (EDS) were used for phase composition determination. Four three-phase equilibria and four two-phase equilibria have been experimentally determined at both isothermal sections of 300 and 350 degrees C. The phase equilibria relationships in the Mg-rich side were studied. The major invariant reaction temperatures of vertical sections with 80 at. % Mg and 10 at. % Sr were determined with differential scanning calorimetry (DSC) test. Moreover, thermodynamic modeling of Mg-Nd-Sr ternary system has been carried out by CALPHAD method based on the present key experimental results. The liquid solution was described using the modified quasi-chemical model in the pair approximation (MQMPA). The compound energy formalism (CEF) was used for the solid phases. The present obtained thermodynamic database of Mg-Nd-Sr ternary system will provide an important support for the Mg-based biodegradable implant development.