Stability and wettability of ternary carbide Mo2Ga2C in molten metals

被引：2
|
作者：
Du, Yaqiong [1 ]
Wang, Fengling [1 ]
Hu, Meihua [1 ]
Hu, Qianku [1 ]
Zhou, Aiguo [1 ]
机构：
[1] Henan Polytech Univ, Sch Mat Sci & Engn, Jiaozuo 454003, Henan, Peoples R China
来源：
CERAMICS INTERNATIONAL | 2023年 / 49卷 / 13期
基金：
中国国家自然科学基金;
关键词：
Mo2Ga2C; Molten metals; Stability; Wettability; MAX phase; IN-SITU DIFFRACTION; TEMPERATURE; DECOMPOSITION; MECHANISMS; BEHAVIOR; HARDNESS; TI3SIC2; GROWTH; TI2SNC; GA;
D O I：
10.1016/j.ceramint.2023.03.275
中图分类号：
TQ174 [陶瓷工业]; TB3 [工程材料学];
学科分类号：
0805 ; 080502 ;
摘要：
Mo2Ga2C is a novel member of MAX phases, which is a family of ternary carbide/nitride with layered structure. The stability and wettability of Mo2Ga2C in molten metals are crucial for the application of Mo2Ga2C in the field of composite materials. In this work, the stability and wettability of Mo2Ga2C in three molten metals (Pb, Sn and Zn) were investigated. Mo2Ga2C was mixed with metal powders and annealed at different temperatures under vacuum. At 700 degrees C, Mo2Ga2C was not stable in any of the three molten metals. The decomposition of Mo2Ga2C was affected by the type of metal matrix as well as the reaction temperature. Mo2Ga2C decomposed at 550 degrees C in Pb, at 450 degrees C in Sn, or at 650 degrees C-750 degrees C in Zn. To characterized the wettability of these metals with Mo2Ga2C, the contact angle of molten metals with Mo2Ga2C at 650 degrees C were measured, which are 103 degrees for Pb, 126 degrees for Sn and 0 degrees for Zn, respectively. Mo2Ga2C has good wettability with Zn and is not wetted by Pb and Sn.
引用
收藏
页码：21449 / 21454
页数：6
相关论文
共 50 条
  • [31] Wettability of Solid Metals by Molten MnO-SiO2 Slag
    G. Parry
    O. Ostrovski
    Metallurgical and Materials Transactions B, 2008, 39 : 669 - 680
  • [32] Wettability of Solid Metals by Molten MnO-SiO2 Slag
    Parry, G.
    Ostrovski, O.
    METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 2008, 39 (05): : 669 - 680
  • [33] ORDERING IN CARBIDE MO2C
    KHAENKO, BV
    VELIKANOVA, TY
    KUBLIJ, VZ
    DOPOVIDI AKADEMII NAUK UKRAINSKOI RSR SERIYA A-FIZIKO-MATEMATICHNI TA TECHNICHNI NAUKI, 1986, (10): : 78 - 82
  • [34] Wettability　of　Monocrystalline　Silicon　Carbide　by　Molten　Metals　and　Binary　Metal－Silicon　Alloys
    李建国
    RARE METALS, 1995, (02) : 96 - 105
  • [35] TERNARY CARBIDE SYSTEMS OF HIGH MELTING TRANSITIONAL METALS .2.
    HOLLECK, H
    METALL, 1981, 35 (12): : 1246 - 1253
  • [36] ORDERED MODIFICATION OF CARBIDE MO2C
    KHAENKO, BV
    KUBLY, VZ
    VELIKANOVA, TY
    DOPOVIDI AKADEMII NAUK UKRAINSKOI RSR SERIYA A-FIZIKO-MATEMATICHNI TA TECHNICHNI NAUKI, 1985, (01): : 80 - 83
  • [37] Wettability of Solid Metals by Molten CaO-SiO2-Al2O3 Slag
    Parry, G.
    Ostrovski, O.
    METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 2008, 39 (05): : 681 - 689
  • [38] Wettability of Solid Metals by Molten CaO-SiO2-Al2O3 Slag
    G. Parry
    O. Ostrovski
    Metallurgical and Materials Transactions B, 2008, 39 : 681 - 689
  • [39] Phase stability of the nanolaminates V2Ga2C and (Mo1-xVx)2Ga2C from first-principles calculations
    Thore, A.
    Dahlqvist, M.
    Alling, B.
    Rosen, J.
    PHYSICAL CHEMISTRY CHEMICAL PHYSICS, 2016, 18 (18) : 12682 - 12688
  • [40] THE STRUCTURE OF THE TERNARY CARBIDE HO2CR2C3
    BEHRENS, RK
    JEITSCHKO, W
    ACTA CRYSTALLOGRAPHICA SECTION A, 1984, 40 : C238 - C239
12345