Mixing uniformity effect on leaching behaviour of cement-based solidified contaminated clay

Mixing uniformity is essential for the quality control of the contaminated clay's solidification. To investigate the effect of the mixing uniformity on the leaching behaviour of the cement-based solidified contaminated clay, this study proposed a quantitative method to characterize the mixing uniformity and investigated the leaching behaviour by the leaching toxicity tests and semi-dynamic leaching tests. X-ray computed tomography (X-CT) was employed to reveal the internal mesoscopic structure. In this case, Pb2+ was selected as a tagged pollutant because of the widespread attention at heavy metal-contaminated sites. The leaching toxicity indicates the significant Pb2+ concentration deviation among the parallel specimens and non-association with the mixing uniformity. However, the Pb2+ cumulative leaching mass and observed diffusion coefficient by the semi-dynamic leaching tests both decrease with the mixing uniformity. X-CT image analysis reveals that the high cement zones wrap the low cement zones with different dimensions in the heterogeneous solidified matrix. Moreover, the specimen pretreatment method in the existing leaching toxicity standards may be inadequate because of the overall encapsulation destruction by the crushing process and representativeness uncertainty when sampling. However, for semi-dynamic leaching, the Pb2+ migration depends on the uniformity, reflecting the continuous distribution of high cement zones.