Corrosion mechanism and fatigue behavior of aluminum alloy with high silicon content

被引：3
|
作者：
Shui, Youfu [1 ]
Liu, Jinxiang [1 ]
Huang, Weiqing [1 ]
Zhao, Nuo [2 ]
Ren, Peirong [1 ]
Zhao, Chengzhang [1 ]
机构：
[1] Beijing Inst Technol, Sch Mech Engn, Beijing 100081, Peoples R China
[2] China Shipbuilding Informat Ctr, Beijing 100101, Peoples R China
来源：
MATERIALS CHEMISTRY AND PHYSICS | 2023年 / 296卷
关键词：
Al-8Si alloy; Pitting corrosion; Intergranular corrosion; Dislocation energy; Corrosion fatigue; INTERGRANULAR CORROSION; SI ALLOYS; AL; MICROSTRUCTURE; PRECIPITATION; LONG; ROOM;
D O I：
10.1016/j.matchemphys.2022.127211
中图分类号：
T [工业技术];
学科分类号：
08 ;
摘要：
The corrosion and corrosion-assisted fatigue life degradation behaviors of Al-8Si alloy is investigated. The test results show that galvanic cells are formed in the inter-dendrites due to high Si concentration, leading to pitting corrosion. The Al2Cu phase and the Si-rich phase precipitate at the grain boundaries in the inter-dendrites, among which the Al2Cu phase is the most critical factor leading to intergranular corrosion. Subsequently, intergranular corrosion gradually develops into intragranular corrosion attributed to the higher dislocation energy in fine-grained Al grains. Additionally, it is found by comparing the corrosion potential and corrosion rate that high Si concentration would cause the decrease in corrosion resistance. Finally, the fatigue test results show that the corrosion could reduce fatigue life of Al-8Si alloy by 79.77% on average. Therefore, the corrosion -induced fatigue life degradation is very worth to be considered in structures.
引用
收藏
页数：10
相关论文
共 50 条
  • [21] Localized corrosion behavior of aluminum-magnesium-silicon alloy in ground water
    Sato, F
    Asakawa, Y
    CORROSION, 1999, 55 (05) : 522 - 529
  • [22] Corrosion behavior of a newly developed high strength aluminum alloy with high magnesium content under simulated seawater environment
    Lv, Xiaodan
    Liu, Shuhui
    Xie, Hui
    Cao, Qingmin
    Zhang, Chengdong
    Chen, Fanwei
    Liu, Bin
    MATERIALS AND CORROSION-WERKSTOFFE UND KORROSION, 2022, 73 (08): : 1318 - 1329
  • [23] Fretting Fatigue Behavior of Aluminum Alloy
    Jayaprakash, M.
    Achyuth, Kulkarni
    Patel, Mahesh
    Sangral, Sangam
    STRUCTURAL INTEGRITY ASSESSMENT, ICONS 2018, 2020, : 683 - 690
  • [24] Effects of silicon content on microstructure and stress corrosion cracking resistance of 7050 aluminum alloy
    She, Huan
    Chu, Wei
    Shu, Da
    Wang, Jun
    Sun, Bao-de
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2014, 24 (07) : 2307 - 2313
  • [25] CORROSION FATIGUE MECHANISM ON HOT-FORGED AA6082 ALUMINUM ALLOY
    Saleema, N.
    Gauthier, P.
    Chen, X. -G.
    PROCEEDINGS OF THE 13TH INTERNATIONAL CONFERENCE ON ALUMINUM ALLOYS (ICAA13), 2012, : 397 - 403
  • [26] Hydrogen content and porosity behavior of hypereutectic aluminum-silicon alloy with phosphorus
    Hu, LN
    Bian, XF
    Duan, YF
    JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION, 2004, 19 (04): : 65 - +
  • [27] Corrosion fatigue crack propagation behavior of LY12CZ aluminum alloy
    Huang, X. G.
    Han, Z. Y.
    Feng, G. T.
    ADVANCED MATERIALS, MECHANICAL AND STRUCTURAL ENGINEERING, 2016, : 17 - 21
  • [28] Research on the microstructure, fatigue and corrosion behavior of permanent mold and die cast aluminum alloy
    Hu, Zuqi
    Wan, Li
    Lu, Shulin
    Zhu, Peng
    Wu, Shusen
    MATERIALS & DESIGN, 2014, 55 : 353 - 360
  • [29] THE EFFECT OF CATHODIC POLARIZATION ON THE CORROSION FATIGUE BEHAVIOR OF A PRECIPITATION HARDENED ALUMINUM-ALLOY
    SMITH, EF
    DUQUETTE, DJ
    METALLURGICAL TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1986, 17 (02): : 339 - 347
  • [30] Corrosion-fatigue behavior of welded aluminum alloy 2024-T3
    Yadav, V. K.
    Gaur, V.
    Singh, I. V.
    INTERNATIONAL JOURNAL OF FATIGUE, 2023, 173
12345