Effects of Sodium Tripolyphosphate Addition on the Dispersion and Hydration of Pure Calcium Aluminate Cement

In this paper, the effect of a sodium tripolyphosphate (STPP) addition on the dispersion and hydration of pure calcium aluminate cement (PCAC) was investigated, and the corresponding mechanism of effect was studied. The effects of STPP on the dispersion, rheology, and hydration processes of PCAC and its adsorption capacity on the surface of cement particles were analysed by measuring the zeta-potential on the surface of cement particles, the changes in the concentrations of elemental P and Ca2+ ions in a solution at different STPP additions. The experimental results show that STPP easily complexes with Ca2+ ions to produce the complex [CaP3O10](3-) adsorbed on the surface of cement particles, which changes the potential on the surface of cement particles and increases the electrostatic repulsive force between cement particles, thus improving the dispersion and rheology of cement. At the same time, the contact area between cement particles and water is reduced, which hinders the hydration process and makes the time of hydration process longer. A comprehensive analysis shows that the best effect of STPP on pure calcium aluminate cements is achieved when the addition of STPP is 0.2%. This study can provide a reference for the addition of water-reducing agents in refractory castables as well as improving the quality of refractory materials.