Preparation of Ni/PZT Core-shell Nanoparticles and Their Electromagnetic Properties

被引：0

作者：

范桂芬 ^{[1
,2
]}

XU Xing ^{[1
,2
]}

WANG Xiaochuan ^{[1
,2
]}

LU Wenzhong ^{[1
,2
]}

LIANG Fei ^{[1
,2
]}

WANG Kai ^{[1
,2
]}

机构：

[1] School of Optical and Electronic Information, Huazhong University of Science and Technology

[2] Key Lab of Functional Materials for Electronic Information, MOE, Huazhong University of Science and Technology

来源：

Journal of Wuhan University of Technology(Materials Science) | 2018年 / 33卷 / 01期

基金：

中国国家自然科学基金;

关键词：

Ni nanoparticles; sol-gel method; in situ reaction; PZT coating layer; electromagnetic property;

D O I：

暂无

中图分类号：

TB383.1 [];

学科分类号：

070205 ; 080501 ; 1406 ;

摘要：

The Ni nanoparticles coated with Pb(Zr,Ti)O3(PZT) were synthesized by a sol-gel method and in situ reaction. And their structure, oxidation resistance, and electromagnetic properties were investigated. The X-ray diffraction patterns(XRD) exhibited that a small amount of impure phase characterized to Ni(OH)2was detected from the ammonia-treated Ni nanoparticles and the ammonia-treated Ni nanoparticles coated with PZT. After being pre-treated with aqueous ammonia, the PZT coating layer was more uniform and about 10 nm in thickness. The oxidation resistance of the ammonia-treated Ni nanoparticles coated with PZT, compared with that of the non-treated ones, was improved by about 66 ℃. The PZT shell layer prepared by in-situ reaction can greatly reduce the dielectric constant and improve the natural resonance loss at high frequency, so as to obtain the optimal impedance matching performance of the electromagnetic wave transmission.

引用

页码：9 / 14

页数：6

共 50 条

[41] Electromagnetic properties of resonant magnetoplasmonic core-shell nanostructures
Mezeme, M. Essone
Lasquellec, S.
Brosseau, C.
JOURNAL OF APPLIED PHYSICS, 2011, 109 (01)
[42] Preparation of Ni/C Core-shell Nanoparticles through MOF Pyrolysis for Phenylacetylene Hydrogenation Reaction
Guo Xiaoling
Chen Xiao
Su Dangsheng
Liang Changhai
ACTA CHIMICA SINICA, 2018, 76 (01) : 22 - 29
[43] Preparation and Antibacterial Properties of the Core-Shell Structure SiO2@Ag Nanoparticles
Liu, Aixin
Sun, Lei
Zhao, Yanbao
Zhang, Zhijun
CURRENT NANOSCIENCE, 2012, 8 (06) : 861 - 867
[44] Structure and deformations of Pd-Ni core-shell nanoparticles
Sao-Joao, S
Giorgio, S
Penisson, JM
Chapon, C
Bourgeois, S
Henry, C
JOURNAL OF PHYSICAL CHEMISTRY B, 2005, 109 (01): : 342 - 347
[45] Smooth surface polypyrrole-silica core-shell nanoparticles: Preparation, characterization and properties
Marini, Michele
Pilati, Francesco
Pourabbas, Behzad
MACROMOLECULAR CHEMISTRY AND PHYSICS, 2008, 209 (13) : 1374 - 1380
[46] Preparation and Characterization of Core-Shell PS/Ni Composite Microspheres
Zhao, Wen
Zhang, Qiuyu
Zhang, Junping
Gu, Junwei
Guo, Feige
POLYMER COMPOSITES, 2009, 30 (08) : 1098 - 1105
[47] Studies on preparation and properties of PAA/gelatin core-shell nanoparticles via template polymerization
Wang, Yansong
Zhang, Youwei
Wu, Chengxun
Zhao, Jiongxin
POLYMER, 2007, 48 (20) : 5950 - 5959
[48] Preparation of Au@SiO2 Core-Shell Nanoparticles: Controlling the Optical Properties
Tan En-zhong
Yin Peng-gang
Huang Wei-feng
Yu Ge
Yu Chun-na
SPECTROSCOPY AND SPECTRAL ANALYSIS, 2012, 32 (12) : 3267 - 3270
[49] Preparation and properties of a core-shell hydrogel loaded with yeast and TiO2 nanoparticles
Song, Ge
Zhang, Min
Song, Jie
Kanwal, Aqsa
Li, Chengtao
Jingxi Huagong/Fine Chemicals, 2021, 38 (03): : 518 - 524
[50] Preparation of iron boride-silica core-shell nanoparticles with soft ferromagnetic properties
Saiyasombat, C.
Petchsang, N.
Tang, I. M.
Hodak, J. H.
NANOTECHNOLOGY, 2008, 19 (08)

← 1 2 3 4 5 →