CORROSION FATIGUE CRACK GROWTH OF MEDIUM STRENGTH STEEL HT60 IN SYNTHETIC SEA WATER

被引：0
|
作者：
GAO Hongbin
机构：
来源：
Acta Metallurgica Sinica(English Edition) | 1992年 / 07期
关键词：
corrosion fatigue; crack growth; crack closure; synthetic seawater;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The corrosion fatigue crack growth and near-threshold characteristics of a medium strengthsteel HT60 were investigated using compact tension specimens exposed to synthetic sea water.The da/dN-△AKrelation in air can give a conservative estimation of da/dN-△K relationsin sea water. In the case of high R, however, crack growth acceleration at high △K regionsappears to be cantrolled by the stress-assisted dissolution. The crack opening stressinlensity factor Kdetected by the back-face-strain method is the result of crack surface incontact with the corrosion products and therefore an overestimated value of Kat the cracktip is given.
引用
收藏
页码：48 / 52
页数：5
相关论文
共 50 条
  • [31] Corrosion fatigue crack growth of AISI 4340 steel
    Weng, Lin
    Zhang, Jixi
    Kalnaus, Sergiy
    Feng, Miaoling
    Jiang, Yanyao
    INTERNATIONAL JOURNAL OF FATIGUE, 2013, 48 : 156 - 164
  • [32] EFFECT OF CATHODIC PROTECTION ON CORROSION FATIGUE BEHAVIOR OF CARBON STEEL IN SYNTHETIC SEA WATER
    HUDGINS, CM
    CASAD, BM
    SCHROEDE.RL
    PATTON, CC
    JOURNAL OF PETROLEUM TECHNOLOGY, 1971, 23 (MAR): : 283 - &
  • [33] EFFECT OF CATHODIC POTENTIAL ON CORROSION-FATIGUE CRACK GROWTH IN A516-60 STEEL
    SULLIVAN, AM
    CROOKER, TW
    REPORT OF NRL PROGRESS, 1976, (OCT): : 5 - 6
  • [34] CORROSION FATIGUE CRACK GROWTH IN HIGH TENSILE STRENGTH STEEL UNDER CATHODIC OVERPROTECTION.
    Komai, Kenjiro
    Minoshima, Kohji
    Yamamoto, Kazutoshi
    Zairyo/Journal of the Society of Materials Science, Japan, 1984, 33 (374) : 1407 - 1413
  • [35] Computer simulation study of the effect of the electrical field on the corrosion fatigue crack growth rate of anodically polarized steel in sea water
    van der Wekken, CJ
    Janssen, M
    PROGRESS IN MECHANICAL BEHAVIOUR OF MATERIALS (ICM8), VOL 1: FATIGUE AND FRACTURE, 1999, : 370 - 374
  • [36] CRACK NUCLEATION AND PROPAGATION OF CORROSION FATIGUE IN HIGH-STRENGTH STEEL
    HIROSE, Y
    MURA, T
    ENGINEERING FRACTURE MECHANICS, 1985, 22 (05) : 859 - 870
  • [37] Influence of temperature, cyclic frequency, and steel strength on surface fatigue crack growth behavior of low and high carbon steel wires in sea water
    Suzuki, Yohnosuke
    Motoda, Shin-Ichi
    Ito, Fumio
    Tsujikawa, Shigeo
    Zairyo to Kankyo/ Corrosion Engineering, 2002, 51 (11): : 502 - 509
  • [38] Fatigue crack propagation under corrosion of high-strength steel
    Malikova, Lucie
    Doubek, Pavel
    Juhaszova, Tereza
    Krejsa, Martin
    Seitl, Stanislav
    10TH INTERNATIONAL CONFERENCE ON MATERIALS STRUCTURE AND MICROMECHANICS OF FRACTURE, MSMF, 2023, 43 : 264 - 269
  • [39] ELECTROCHEMICAL CONDITIONS AT THE CRACK TIP AND CRACK PROPAGATION RATES DURING CORROSION FATIGUE OF STEEL IN DEAERATED SEA WATER.
    van der Wekken, C.J.
    Zuidema, J.
    Key Engineering Materials, 1987, 20-28 (pt 1-4)
  • [40] Corrosion fatigue crack growth inhibition of duplex stainless steel
    Ahsan, M
    Gasem, Z
    DAMAGE AND FRACTURE MECHANICS VIII: COMPUTER AIDED ASSESSMENT AND CONTROL, 2004, 14 : 59 - 68
12345