Glass-Forming Ability for Nd70-xFe20Al10Yx and Nd60-xFe30Al10Yx Alloys

被引：0
|
作者：
Keqiang QIU
机构：
来源：
JournalofMaterialsScience&Technology | 2003年 / 02期
关键词：
Nd-based alloys; Glass forming ability; Liquidus temperature; Thermal stability;
D O I：
暂无
中图分类号：
TG13 [合金学与各种性质合金];
学科分类号：
080502 ;
摘要：
The glass-forming ability (GFA) of Nd70-xFe2oAl10Yx and Nd60-xFe30Al10Yx (0< x <15) alloys produced by Cu mold casting was investigated. Except Y=5 at. pct, bulk amorphous Nd70-xFe20Al10Yx alloys up to 2 mm in diameter were obtained. The GFA for Nd60-xFe30Al10Yx alloys, however, was found to decrease with increase of Y due to the increasing compositional deviation from the original eutectic point of Nd60Fe30Al10 alloy. The Nd60Fe20Al10Y10 and Nd60Fe30Al10 alloy exhibit the largest GFA and can be cast into bulk amorphous cylindrical specimens of 3 mm in diameter. The melting temperature or/and the reduced crystallization temperature is closely related to the GFA of Y-containing alloys. The bulk amorphous cylinder for the Nd55Fe20Al10Y15 alloy shows a distinct glass transition temperature and a wide supercooled liquid region before crystallization. The crystallization temperature, Tg, and the supercooled liquid region, TX, are 776 K and 58 K, respectively. The GFA and thermal stability of the Nd-Fe-AI-Y a
引用
收藏
页码：102 / 106
页数：5
相关论文
共 50 条
  • [31] Glass-Forming Ability and Corrosion Resistance of Al88Y8-xFe4+x (x=0, 1, 2 at.%) Alloys
    Babilas, Rafal
    Spilka, Monika
    Mlynarek, Katarzyna
    Lonski, Wojciech
    Lukowiec, Dariusz
    Radon, Adrian
    Kadziolka-Gawel, Mariola
    Gebara, Piotr
    MATERIALS, 2021, 14 (07)
  • [32] Magnetic Characteristics for the Mould-Cast Hard Magnetic Nd70-xFe30Alx (x=0-10) Alloys
    Zhao, Lizhong
    Zheng, Zhigang
    Chen, Xi
    Qiu, Zhaoguo
    Lai, Jiawei
    Wang, Gang
    Liu, Zhongwu
    Ramanujan, Raju V.
    IEEE TRANSACTIONS ON MAGNETICS, 2015, 51 (08)
  • [33] Magnetic Properties and Coercivity Mechanism in the (Nd0.7Pr0.3)60-xFe30Al10Cux (x=0, 1, 2, 4) Bulk Amorphous Alloys
    Tang Yongjun
    Xu Hui
    Hou Xueling
    RARE METAL MATERIALS AND ENGINEERING, 2015, 44 (03) : 634 - 637
  • [34] Nd60Fe30Al10 Glass Forming Magnetic Alloys: a Mechanical Spectroscopy Study at the 300-560 K Temperature Range
    Salva, H. R.
    Ghilarducci, A. A.
    Urreta, S. E.
    Fabietti, L. M.
    Levingston, J. M.
    INTERNAL FRICTION AND MECHANICAL SPECTROSCOPY, 2012, 184 : 426 - +
  • [35] Mechanical spectroscopy studies of partially amorphous Nd60Fe30Al10 alloys
    Tarnowski, GC
    Salva, H
    Ghilarducci, AA
    Urreta, SE
    Billoni, OV
    Fabietti, LM
    PHYSICA B-CONDENSED MATTER, 2004, 354 (1-4) : 220 - 223
  • [36] Large unidirectional anisotropy in Nd60Fe30Al10 bulk amorphous alloys
    Hong, NM
    Dan, NH
    Phuc, NX
    JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 2002, 242 : 847 - 849
  • [37] Glass-forming ability and thermal stability of bulk Zr55Al10Cu30Ni5-xPdx amorphous alloys
    Qin, FX
    Zhang, HF
    Li, H
    Ding, BZ
    Hu, ZQ
    ACTA METALLURGICA SINICA, 2003, 39 (03) : 305 - 309
  • [38] Cooling rate-dependent microstructure and magnetic properties of the glass forming alloy Nd60Fe30Al10
    Bracchi, A
    Schneider, S
    Thiyagarajan, P
    Samwer, K
    JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS, 2004, 272 : 1423 - 1424
  • [39] Cooling rate induced variation in microstructure and magnetic structure of Nd60Fe30Al10 glass forming alloy
    Hu, Y.
    Chan, K. C.
    Liu, L.
    Yang, Y. Z.
    MATERIALS LETTERS, 2007, 61 (18) : 3909 - 3912
  • [40] Thermal stability and glass-forming ability of amorphous Nd-Al-TM (TM=Fe, Co, Ni or Cu) alloys
    Inoue, A
    Zhang, T
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 1997, 226 : 393 - 396
12345