Effect of temperature and stress on high temperature creep behavior of Ni3Al-based single crystal superalloy

被引：0

作者：

Cheng Chang ^{[1
]}

Liwu Jiang ^{[1
]}

Meiling Wu ^{[2
]}

Shusuo Li ^{[3
]}

Yafang Han ^{[2
]}

机构：

[1] National Center for Materials Service Safety, University of Science and Technology Beijing

[2] Beijing Institute of Aeronautical Materials

[3] Research Institute of Aero-engine, Beihang University

来源：

ProgressinNaturalScience:MaterialsInternational | 2022年 / 32卷 / 02期

基金：

中国国家自然科学基金;

关键词：

D O I：

暂无

中图分类号：

TG132.3 [特种热性质合金];

学科分类号：

摘要：

The creep behavior and dislocations mechanism of the Ni3Al-based single crystal alloy IC6 SX with [001] orientation were investigated under the testing conditions of 1100℃/137 MPa,1100℃/120 MPa and 1070℃/137 MPa.It was observed that the temperature and stress had a significant effect on the high temperature creep life of the single crystal alloy.As the temperature was reduced from 1100℃ to 1070 ℃,the creep life increased from65.07 h to 313.8 h.As the stress was reduced to 120 MPa,the creep life increased to 243.3 h.Under the high temperature and low stress condition the dislocations entered the γ’ phase by climbing caused by the atomic diffusion,instead of slipping.

引用

页码：267 / 271

页数：5

共 50 条

[31] A comparative study of four modified Al coatings on Ni3Al-based single crystal superalloy
Wu, Qiong
Yang, Rui-bo
Wu, Yu-xiao
Li, Shu-suo
Ma, Yue
Gong, Sheng-kai
PROGRESS IN NATURAL SCIENCE-MATERIALS INTERNATIONAL, 2011, 21 (06) : 496 - 505
[32] Study on the Creep Behavior of a Ni3Al-Based Single Crystal Alloy at 850°C/450 MPa
Jiang, Liwu
Yang, Yu
Wu, Meiling
Cai, Min
INTERNATIONAL JOURNAL OF PHOTOENERGY, 2020, 2020
[33] Very high temperature creep behavior of a single crystal Ni-based superalloy under complex thermal cycling conditions
Cormier, J.
Jouiad, M.
Hamon, F.
Villechaise, P.
Milhet, X.
PHILOSOPHICAL MAGAZINE LETTERS, 2010, 90 (08) : 611 - 620
[34] Kinetics and microstructural evolution during recrystallization of a Ni3Al-based single crystal superalloy
Wu Yu-xiao
Zhang Heng
Li Fu-lin
Li Shu-suo
Gong Sheng-kai
Han Ya-fang
TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2012, 22 (09) : 2098 - 2105
[35] Low temperature and rapid diffusion bonding of Ni3Al-based superalloy with Ni-based superalloy by spark plasma sintering
Wu, Tong
Wang, Ce
Yang, Jia
Xu, Rui
Xue, Xiaoqian
Fu, Mengchun
Zhao, Yuwei
Xu, Jiujie
Zhang, Qiuguang
Lin, Panpan
Yue, Xin
Lin, Tiesong
He, Peng
JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2024, 326
[36] Study on microstructure evolution and failure behavior of Ni3Al-based single crystal superalloy joints brazed with Ni-based filler
Cao, Yang
Hu, Bin
Liu, Qiaomu
Geng, Lilun
Du, Boxuan
Hu, Yunpeng
Zhang, Heng
Pei, Yanling
Li, Shusuo
Gong, Shengkai
JOURNAL OF MATERIALS RESEARCH AND TECHNOLOGY-JMR&T, 2024, 30 : 7171 - 7186
[37] ANISOTHERMAL HIGH-TEMPERATURE CYCLIC BEHAVIOR OF A Ni-BASED SINGLE CRYSTAL SUPERALLOY
le Graverend, Jean-Briac
Cormier, Jonathan
Gallemeau, Franck
Kruch, Serge
Mendez, Jose
PROCEEDINGS OF THE 13TH INTENATIONAL SYMPOSIUM OF SUPERALLOYS (SUPERALLOYS 2016), 2016, : 647 - 654
[38] High Temperature Creep Behavior and Fracture Characteristics of a 2% Ru Nickel Based Single Crystal Superalloy
Liang, Shuang
Tian, Sugui
Liu, Zhixin
Shu, Delong
HIGH PERFORMANCE STRUCTURAL MATERIALS, 2018, : 599 - 607
[39] Creep and damage behavior of containing Mo nickel-based single crystal superalloy at high temperature
Liang S.
Tian S.-G.
Liu Z.-X.
Xue Y.-C.
Tian, Su-Gui (tiansugui2003@163.com), 1600, Central South University of Technology (27): : 911 - 919
[40] Effect of heat treatment and long-term age on microstructure of a Ni3Al-based single crystal superalloy
Ai, C.
Ou, M. Q.
Zhao, X. B.
Pei, Y. L.
Zhang, H.
Liu, L.
Li, S. S.
Gong, S. K.
MATERIALS RESEARCH INNOVATIONS, 2015, 19 : S209 - S213

← 1 2 3 4 5 →