Preparation of Long-Lasting Phosphorescence (LLP) Glass-Ceramic Materials

Three kinds of glass-ceramics, i.e., Mn 2+ doped zinc borosilicate, Eu 2+, Dy 3+ co-doped strontium aluminoborate and Eu 2+, Nd 3+ co-doped calcium aluminoborate were prepared, whose phosphorescence emission band peaks at 525, 516 and 464 nm, respectively. In preparation of these glass-ceramics the base glasses were gained by heating the mixed starting materials at high temperature to get the transparent glasses; then those glasses were heat-treated and turned to opaque glass-ceramics. X-ray diffraction (XRD) shows that the crystallites are ZnSiO 4, SrAl 2O 4 and α-CaAl 2B 2O 7, respectively. It is a useful way to get new LLP materials by the method reported in this work that may be considered as “from glass to crystal”.