SELF-ASSEMBLY OF ROD-COIL DIBLOCK COPOLYMERS——INFLUENCE OF THE ROD LENGTH

The self-assembly of five narrowly distributed novel rod-coil diblock copolymers, poly(styrene-block-(2, 5-bis[4-methoxy-phenyl]oxycarbonyl) styrene) (PS-b-PMPCS), in p-xylene, a selective solvent at room temperature, was studied. Therod-coil copolymers, which have the same PS length but different PMPCS length, were synthesized by 2,2,6,6-tetramethyl-I-piperidinyloxy (TEMPO) mediated living free radical polymerization. The influence of the rod length on the self-assemblymorphology was studied by transmission electron microscopy (TEM). At a concentration of 2.0 mg/mL, those copolymerswith relatively shorter PMPCS length (copolymers 1 and 2) form individual spherical micelles; those with relatively longerPMPCS length (copolymer 3 and 4) form "pearl chains" coexisting with individual spherical micelles; the ones with longestPMPCS length form "pearl chains" coexisting with occasionally formed nanofibers. The diameter of all the morphologieswas controlled by the rod length. This gives us a way to govern the self-assembly morphology by altering the length of oneblock in the block copolymer.