Wear behavior and nano-structure of surface layers of Hadfield steel under impact loading

被引：0
|
作者：
许云华
陈瑜眉
朱金华
机构：
[1] China
[2] China Institute of Wear Resistance Materials
[3] State Key Laboratory for Mechanical Behavior of Materials
[4] Xi’an 710055
[5] Xi’an Jiaotong University
[6] Xi’an University of Architecture and Technology
[7] Xi’an710049
来源：
ProgressinNaturalScience | 2001年 / 06期
基金：
中国国家自然科学基金;
关键词：
Hadfield steel; impact wear; nano-sized grains; amorphous structure;
D O I：
暂无
中图分类号：
TG174 [腐蚀的控制与防护];
学科分类号：
摘要：
Under high energy impact contact loading, a turning on the weight loss-impact cycle ( WL-N) curve has been found, which results from the formation of nano-sized grains embedded in amorphous in the surface layers of Hadfield steel. As the impact energy increases, the wear rate, dWL/dN, first increases then decreases. The nano-structure due to the accumulation of plastic deformation is composed of nano-sized grains spanning 10 - 50 atoms and amorphous structures.
引用
收藏
页码：49 / 55
页数：7
相关论文
共 50 条
  • [41] Effect of Aluminum on the Structural Transitions and the Wear Resistance of Hadfield Steel under Friction
    L. G. Korshunov
    N. L. Chernenko
    Physics of Metals and Metallography, 2018, 119 : 700 - 706
  • [42] Multiphase steel with improved impact-abrasive wear resistance in comparison with conventional Hadfield steel
    Wang, Wei
    Song, Renbo
    Peng, Shiguang
    Pei, Zhongzheng
    MATERIALS & DESIGN, 2016, 105 : 96 - 105
  • [43] Thermal stability and nano-structure of metal-doped carbon layers
    Balden, M.
    Adelhelm, C.
    Sikora, M.
    JOURNAL OF NUCLEAR MATERIALS, 2007, 367 (SPEC. ISS.) : 1458 - 1462
  • [44] Coexistance of Cu and Ag in surface nano-structure and the new behavior of glycine adsorption on silver surfaces
    Ge, SP
    Zhu, X
    Yang, WS
    ACTA PHYSICA SINICA, 2004, 53 (10) : 3447 - 3452
  • [45] ON WEAR THICKNESS OF RUST LAYERS OF STEEL STRUCTURE DUE TO ICE IMPACT LOAD
    Takeuchi, Takahiro
    Kioka, Shinji
    Miyazaki, Hitoshi
    PROCEEDINGS OF ASME 2023 42ND INTERNATIONAL CONFERENCE ON OCEAN, OFFSHORE & ARCTIC ENGINEERING, OMAE2023, VOL 6, 2023,
  • [46] Grain coarsening of nano laminated structure in martensite steel under sliding wear
    Gao, Qing-Yuan
    Li, Shu-Xin
    Su, Yun-Shuai
    Cao, Jun
    Moliar, Oleksandr
    TRIBOLOGY INTERNATIONAL, 2020, 151
  • [47] Localized vibrons in a molecular nano-structure adsorbed on a vicinal surface
    Pouthier, V
    Girardet, C
    SURFACE SCIENCE, 2002, 502 : 503 - 512
  • [48] Abrasive Wear Behavior of High Chromium Cast Iron and Hadfield Steel-A Comparison
    Atabaki, Mehdi Mazar
    Jafari, Sajjad
    Abdollah-pour, Hassan
    JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL, 2012, 19 (04) : 43 - 50
  • [49] Abrasive Wear Behavior of High Chromium Cast Iron and Hadfield Steel-A Comparison
    Mehdi Mazar Atabaki
    Sajjad Jafari
    Hassan Abdollah-pour
    JournalofIronandSteelResearch(International), 2012, 19 (04) : 43 - 50
  • [50] Surface nano-structure of polyamide 6 film by hydrothermal treatment
    Wang, Xiaosong
    Wang, Zhiliang
    Liang, Songmiao
    Jin, Yan
    Lotz, Bernard
    Yang, Shuguang
    APPLIED SURFACE SCIENCE, 2018, 442 : 595 - 601
12345