Effects of precipitates on fatigue crack growth rate of AA 7055 aluminum alloy

被引：0

作者：

陈军洲 ^{[1
]}

甄良 ^{[2
]}

杨守杰 ^{[1
]}

戴圣龙 ^{[1
]}

机构：

[1] Beijing Institute of Aeronautical Materials

[2] School of Materials Science and Engineering,Harbin Institute of Technology

来源：

Transactions of Nonferrous Metals Society of China | 2010年 / 20卷 / 12期

关键词：

7055 aluminum alloy; ageing; fatigue crack growth rate; precipitate;

D O I：

暂无

中图分类号：

TG146.21 [];

学科分类号：

摘要：

The effects of precipitates on the fatigue crack growth rate of AA 7055 Al alloy subjected to different ageing treatments were investigated using transmission electron microscope and fatigue crack growth testing.The results show that the T77 treated samples exhibit the lowest crack growth rate,while the crack growth rate of over-aged samples is the highest.In terms of the model based on the reversibility of dislocation motion within the plastic zone close to the crack tip,the improved crack growth resistance is attributed to many precipitates that are coherent with Al matrix in the under-aged and T77 treated samples.When the precipitate is coherent with the Al matrix,the larger the precipitate is,the slower the fatigue crack grows.The effects of grain boundary precipitates and precipitate free zone on the fatigue crack growth resistance are less significant than those of precipitates within grains of the alloy.

引用

页码：2209 / 2214

页数：6

共 50 条

[21] Fatigue crack growth rate analysis in a titanium alloy
Korsunsky, Alexander M.
Dini, Daniele
Walsh, Michael J.
ADVANCES IN FRACTURE AND DAMAGE MECHANICS VII, 2008, 385-387 : 5 - +
[22] Effects of different corrosion environments on fatigue property and crack growth rate in 7475-T7351 aluminum alloy
Gong, Yu-Hui
Liu, Ming
Zhang, Kun
Huang, Min
Yi, Lin-Na
Dai, Sheng-Long
Cailiao Gongcheng/Journal of Materials Engineering, 2010, (09): : 71 - 73
[23] Fatigue Crack Growth Behavior in a Rolled Plate of Aluminum Alloy
Ejaz, N.
Muhammad, W.
Salam, I.
ADVANCED MATERIALS XI, 2010, 442 : 283 - 293
[24] FATIGUE CRACK GROWTH ALONG CLEAVAGE PLANES IN AN ALUMINUM ALLOY
THOMPSON, KR
CRAIG, JV
METALLURGICAL TRANSACTIONS, 1970, 1 (04): : 1047 - &
[25] FATIGUE CRACK GROWTH-RETARDATION IN AN ALUMINUM-ALLOY
ROBIN, C
PELLOUX, RM
MATERIALS SCIENCE AND ENGINEERING, 1980, 44 (01): : 115 - 120
[26] Influence of Hydrogen on Fatigue Crack Growth in 7075 Aluminum Alloy
Dey, Swapna
Sivaprasad, Seetharaman
Das, Nityananda
Chattoraj, Indranil
JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2023, 32 (02) : 782 - 792
[27] Analytical and Numerical Investigation of Fatigue Crack Growth in Aluminum Alloy
Golestaneh, AmirrezaFahim
Ali, Aidy
Bayat, M.
FRACTURE AND STRENGTH OF SOLIDS VII, PTS 1 AND 2, 2011, 462-463 : 1050 - +
[28] Fatigue crack growth in an aluminum alloy-fractographic study
Salam, I.
Muhammad, W.
Ejaz, N.
14TH INTERNATIONAL SYMPOSIUM ON ADVANCED MATERIALS (ISAM 2015), 2016, 146
[29] Fatigue crack nucleation and small crack growth in an extruded 6061 aluminum alloy
McCullough, R. R.
Jordon, J. B.
Allison, P. G.
Rushing, T.
Garcia, L.
INTERNATIONAL JOURNAL OF FATIGUE, 2019, 119 : 52 - 61
[30] Influence of Hydrogen on Fatigue Crack Growth in 7075 Aluminum Alloy
Swapna Dey
Seetharaman Sivaprasad
Nityananda Das
Indranil Chattoraj
Journal of Materials Engineering and Performance, 2023, 32 : 782 - 792

← 1 2 3 4 5 →