Low-cycle fatigue lifetime estimation of Ti–6Al–4V welded joints by a continuum damage mechanics model

被引：0

作者：

Hong-Yu Qi ^{[1
]}

Xiao-Lei Zheng ^{[1
]}

Xiao-Guang Yang ^{[1
]}

机构：

[1] School of Energy and Power Engineering,Beihang University

来源：

RareMetals | 2016年 / 35卷 / 04期

关键词：

Electron beam welding; Low-cycle fatigue; Life estimation; Continuum damage mechanics;

D O I：

暂无

中图分类号：

TG407 [焊接接头的力学性能及其强度计算];

学科分类号：

摘要：

The low-cycle fatigue(LCF)behavior of directionally solidified nickel-based superalloy Ti–6Al–4V was studied under bare and electron beam welding conditions at room temperature.Results show that:(1)under the same test conditions,all the joints exhibit lower LCF lifetime than Ti–6Al–4V;(2)the failure of welded structures is mainly ascribed to the welding defect.A novel lifetime prediction methodology based on continuum damage mechanics is proposed to predict the lifetime of Ti–6Al–4V and its welded joints.

引用

页码：299 / 302

页数：4

共 50 条

[41] Continuum damage model for low-cycle fatigue of metals: An overview
Abdul-Latif, Akrum
INTERNATIONAL JOURNAL OF DAMAGE MECHANICS, 2021, 30 (07) : 1036 - 1078
[42] The influence of porosity on the fatigue crack growth behavior of Ti–6Al–4V laser welds
L. W. Tsay
Y.-P. Shan
Y.-H. Chao
W. Y. Shu
Journal of Materials Science, 2006, 41 : 7498 - 7505
[43] Simulation of fatigue small crack growth in additive manufactured Ti–6Al–4V material
A. Gupta
W. Sun
C. J. Bennett
Continuum Mechanics and Thermodynamics, 2020, 32 : 1745 - 1761
[44] Influence of Surface Mechanical Attrition Treatment Duration on Fatigue Lives of Ti–6Al–4V
S. Anand Kumar
S. Ganesh Sundara Raman
T. S. N. Sankara Narayanan
Transactions of the Indian Institute of Metals, 2014, 67 : 137 - 141
[45] Low-cycle fatigue of welded joints: coupled initiation propagation model
Madi, Y
Recho, N
Matheron, P
NUCLEAR ENGINEERING AND DESIGN, 2004, 228 (1-3) : 179 - 194
[46] INVESTIGATION OF HIP REJUVENATION OF THE LOW-CYCLE FATIGUE PROPERTIES OF TI-6AL-4V
CLAUER, AH
LEIS, BN
JOURNAL OF METALS, 1979, 31 (08): : F34 - F34
[47] Effect of Plasma Nitriding Environment and Time on Plain Fatigue and Fretting Fatigue Behavior of Ti–6Al–4V
M. Mubarak Ali
S. Ganesh Sundara Raman
Tribology Letters, 2010, 38 : 291 - 299
[48] Strain behavior of the hydrogenated submicrocrystalline Ti–6Al–4V alloy
E. N. Stepanova
G. P. Grabovetskaya
O. V. Zabudchenko
I. P. Mishin
Russian Physics Journal, 2011, 54 : 690 - 696
[49] Tensile fracture during transformation superplasticity of Ti–6Al–4V
C. Schuh
D. C. Dunand
Journal of Materials Research, 2001, 16 : 865 - 875
[50] LOW-CYCLE AND HIGH-CYCLE FATIGUE RUPTURES AT SAME LOAD IN TI-6AL-4V
MANNONE, G
BRACCO, A
TOSTO, S
METALLOGRAPHY, 1977, 10 (03): : 315 - 335

← 1 2 3 4 5 →