Low-cycle fatigue lifetime estimation of Ti–6Al–4V welded joints by a continuum damage mechanics model

被引：0

作者：

Hong-Yu Qi ^{[1
]}

Xiao-Lei Zheng ^{[1
]}

Xiao-Guang Yang ^{[1
]}

机构：

[1] School of Energy and Power Engineering,Beihang University

来源：

RareMetals | 2016年 / 35卷 / 04期

关键词：

Electron beam welding; Low-cycle fatigue; Life estimation; Continuum damage mechanics;

D O I：

暂无

中图分类号：

TG407 [焊接接头的力学性能及其强度计算];

学科分类号：

摘要：

The low-cycle fatigue(LCF)behavior of directionally solidified nickel-based superalloy Ti–6Al–4V was studied under bare and electron beam welding conditions at room temperature.Results show that:(1)under the same test conditions,all the joints exhibit lower LCF lifetime than Ti–6Al–4V;(2)the failure of welded structures is mainly ascribed to the welding defect.A novel lifetime prediction methodology based on continuum damage mechanics is proposed to predict the lifetime of Ti–6Al–4V and its welded joints.

引用

页码：299 / 302

页数：4

共 50 条

[1] Low-cycle fatigue lifetime estimation of Ti–6Al–4V welded joints by a continuum damage mechanics model
Hong-Yu Qi
Xiao-Lei Zheng
Xiao-Guang Yang
Rare Metals, 2016, 35 : 299 - 302
[2] Low-cycle fatigue lifetime estimation of Ti-6Al-4V welded joints by a continuum damage mechanics model
Qi, Hong-Yu
Zheng, Xiao-Lei
Yang, Xiao-Guang
RARE METALS, 2016, 35 (04) : 299 - 302
[3] Influence of Foreign Object Damage on High Cycle Fatigue of Ti–6Al–4V Alloy
Anuradha Nayak Majila
S. Ramachandra
S. L. Mannan
D. Chandru Fernando
S. N. Narendrababu
Transactions of the Indian Institute of Metals, 2016, 69 : 1475 - 1481
[4] Low cyclic fatigue behavior of electron-beam-welded Ti–6Al–4V titanium joint
Hong-Yu Qi
Li-Qiang Ma
Shao-Lin Li
Xiao-Guang Yang
RareMetals, 2016, 35 (03) : 230 - 234
[5] Low cyclic fatigue behavior of electron-beam-welded Ti–6Al–4V titanium joint
Hong-Yu Qi
Li-Qiang Ma
Shao-Lin Li
Xiao-Guang Yang
Rare Metals, 2016, 35 : 230 - 234
[6] Continuum damage model of low-cycle fatigue and fatigue damage analysis of welded joint
Cheng, GX
Zuo, JZ
Lou, ZW
Kuang, ZB
ENGINEERING FRACTURE MECHANICS, 1996, 55 (01) : 155 - &
[7] Foreign Object Damage Effect on the Fatigue Strength of Ti–6Al–4V Specimens
C. W. Li
X. L. Wu
B. Y. Yang
Q. Chai
Z. P. Zhang
Strength of Materials, 2020, 52 : 587 - 595
[8] A CONTINUUM DAMAGE MECHANICS MODEL FOR LOW-CYCLE FATIGUE FAILURE OF METALS
WANG, J
ENGINEERING FRACTURE MECHANICS, 1992, 41 (03) : 437 - 441
[9] LOW-CYCLE FATIGUE BEHAVIOR OF TI-6AL-4V
WELLS, CH
SULLIVAN, CP
JOURNAL OF METALS, 1968, 20 (01): : A93 - &
[10] Inhomogeneous Fatigue Characteristics of Welded Ti–6Al–4V Thick Plate by the Electron Beam Method
Haiyan Wang
Caiyou Zeng
Yupeng Zhang
Yu Zhou
Chunlin Dong
Metals and Materials International, 2021, 27 : 4527 - 4535

← 1 2 3 4 5 →