Synthesis of porous carbon spheres derived from lignin through a facile method for high performance supercapacitors

Porous carbon spheres（PCS） derived from lignin have been prepared through a facile method and fabricated as electrodes for electric double-layer capacitors. Spherical shaped mixtures of lignosulfonate and crystalized KOH are formed by spray drying of a solution of lignosulfonate and KOH. Activation by KOH is performed at high temperatures along with lignosulfonate carbonization. With an appropriate pore structure, the obtained PCS have a specific surface area of 1372.87 m;g;and show a capacitance of 340 F g;in 3 M KOH at a current density of 0.5 A g;. Moreover, a symmetric supercapacitor fabricated using the PCS as electrodes show a maximum capacitance of 68.5 F g;, and an energy density of 9.7 W h kg;at a power density of 250 W kg;. The capacity retention is more than 94.5% after 5000 galvanostatic chargedischarge cycles. The excellent characteristics seem to be ascribed to the pore structures of PCS that have a large specific surface area and a low electrical resistance.