Evaluation of the Electroslag Remelting Process in Medical Grade of 316LC Stainless Steel

被引：0

作者：

S.Ahmadi ^{[1
]}

H.Arabi ^{[2
]}

A.Shokuhfar ^{[3
]}

A.Rezaei ^{[3
]}

机构：

[1] Institute of Advanced Technologies for Metallic Materials,Tarbiat Modares University

[2] Center of Excellence of Advanced Materials and Processing(CEAMP),Department of Metallurgy and Materials Science and Engineering,Iran University of Science&Technology(IUST)

[3] Department of Material Science,Faculty of Mechanical Engineering,K.N.Toosi University of Technology

来源：

Journal of Materials Science & Technology | 2009年 / 25卷 / 05期

关键词：

Ultra clean steel; Electroslag remelting; Prefused slag; Vertical solidification; Radial solidification;

D O I：

暂无

中图分类号：

TG142.71 [不锈钢、耐酸钢];

学科分类号：

摘要：

This study is focused on the effects of electroslag remelting by prefused slag(CaO,Al2O3,and CaF2)on macrostructure and reduction of inclusions in the medical grade of 316LC(316LVM)stainless steel.Analysis of the obtained results indicated that for production of a uniform ingot structure during electroslag remelting, shape and depth of the molten pool should be carefully controlled.High melting rates led to deeper pool depth and interior radial solidification characteristics,while decrease in the melting rates caused more reduction of nonmetallic inclusions.Large shrinkage cavities formed during the conventional casting process in the primary ingots were found to be the cause of the fluctuation in the melting rate,pool depth and extension of equiaxed crystals zone.

引用

页码：592 / 596

页数：5

共 50 条

[41] Effect of mold rotation on inclusion distribution in bearing steel during electroslag remelting process
Chang Lizhong
Shi Xiaofang
Wang Runxi
Cong Junqiang
Li Tao
CHINA FOUNDRY, 2014, 11 (05) : 452 - 456
[42] Effect of mold rotation on inclusion distribution in bearing steel during electroslag remelting process
Chang Lizhong
Shi Xiaofang
Wang Runxi
Cong Junqiang
Li Tao
China Foundry, 2014, (05) : 452 - 456
[43] The Effect of Al-Mg Deoxidation on the Cleanliness of Steel during the Electroslag Remelting Process
Liu, Weijian
Li, Jing
Wang, Hao
Shi, Chengbin
STEEL RESEARCH INTERNATIONAL, 2019, 90 (10)
[44] Augmentation of crevice corrosion resistance of medical grade 316LVM stainless steel by plasma carburising
Buhagiar, Joseph
Spiteri, Andre
Sacco, Malcolm
Sinagra, Emmanuel
Dong, Hanshan
CORROSION SCIENCE, 2012, 59 : 169 - 178
[45] Enhancement of Corrosion Resistance for Medical Grade 316L Stainless Steel by Electrolytic Plasma Polishing
Gangqiang Ji
Huanwu Sun
Haidong Duan
Dongliang Yang
Jinyan Sun
Journal of Materials Engineering and Performance, 2023, 32 : 1498 - 1507
[46] Alloying of steel with a superequilibrium amount of nitrogen from a gaseous atmosphere in the process of electroslag remelting
Vytvyts'kyi, VI
Tkachov, VI
Hrebenyuk, SO
MATERIALS SCIENCE, 2000, 36 (03) : 454 - 457
[47] ANALYSIS OF OXIDE INCLUSIONS ON MEDICAL GRADE 316L STAINLESS STEEL USING LOCAL RAW
Jujur, I. Nyoman
Sah, Joni
Bakri, Agustanhakri
Wargadipura, Agus Hadi S.
INTERNATIONAL JOURNAL OF TECHNOLOGY, 2015, 6 (07) : 1184 - 1190
[48] Enhancement of Corrosion Resistance for Medical Grade 316L Stainless Steel by Electrolytic Plasma Polishing
Ji, Gangqiang
Sun, Huanwu
Duan, Haidong
Yang, Dongliang
Sun, Jinyan
JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE, 2023, 32 (04) : 1498 - 1507
[49] High-Temperature Oxidation Mechanism of Rack Steel During Electroslag Remelting Process
Xie, Xiangxiang
Li, Wanming
Zang, Ximin
Liu, Baoxi
Liu, Zefeng
METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 2025, : 1792 - 1805
[50] Alloying of steel with a superequilibrium amount of nitrogen from a gaseous atmosphere in the process of electroslag remelting
V. I. Vytvyts’kyi
V. I. Tkachov
S. O. Hrebenyuk
Materials Science, 2000, 36 : 454 - 457

← 1 2 3 4 5 →