Flame-retardant Mechanism of Magnesium Oxychloride in Epoxy Resin

被引：0
|
作者：
秦麟卿
机构：
[1] Center for Material Research and Analysis,Wuhan University of Technology
[2] State Key Laboratory of Advanced Technology for Materials Synthesis and Processing,Wuhan University of Technology
来源：
Journal of Wuhan University of Technology(Materials Science) | 2009年 / 01期
关键词：
magnesium oxychloride; epoxy resin; flame-retardant properties; flame retarded mechanism;
D O I：
暂无
中图分类号：
TQ323.5 [环氧树脂及塑料];
学科分类号：
0805 ; 080502 ;
摘要：
Flame-retardant mechanism of magnesium oxychloride (M OC) in EP was in-vestigated by limiting oxygen index (LOI), XRD, SEM, TG-DTG and DSC. The results show that MOC performed well as an inorganic flame-retardant in EP. When the content of MOC is 50%, the LOI of EP reaches 29.6% and mass of residual char reaches 9.6%. The flame retarde mechanism of MOC is due to the synergies of diluting, cooling, catalyzing char forming and obstructing effects.
引用
收藏
页码：127 / 131
页数：5
相关论文
共 50 条
  • [31] Synthesis and flame-retardant properties of the epoxy resin based on phenanthroline and magnolol
    Xie, Yubin
    Hu, Guoliang
    Zhang, Xiaoqing
    Lei, Caihong
    Fuhe Cailiao Xuebao/Acta Materiae Compositae Sinica, 2024, 41 (12): : 6545 - 6558
  • [32] Research on Performance of Flame-retardant Epoxy Resin Electronic Packaging Materials
    Zhou, Haoran
    Zhao, Shuang
    Yu, Weimiao
    Jiang, Hao
    Guo, Cui
    Li, Ye
    ADVANCED MATERIALS RESEARCHES AND APPLICATION, 2013, 763 : 117 - 120
  • [33] Flame-retardant behaviors of aluminum phosphates coated sepiolite in epoxy resin
    Yan, Wei
    Xie, Pu
    Yang, Zhengwei
    Luo, Guangjin
    Huang, Weijiang
    Tian, Qin
    Tu, Chunyun
    Zhang, Chunmei
    Yang, Chunlin
    Wang, Kui
    JOURNAL OF FIRE SCIENCES, 2021, 39 (01) : 3 - 18
  • [34] Recyclable, malleable and intrinsically flame-retardant epoxy resin with catalytic transesterification
    Chen, Jia-Hui
    Lu, Jia-Hui
    Pu, Xiao-Lu
    Chen, Li
    Wang, Yu-Zhong
    CHEMOSPHERE, 2022, 294
  • [35] Effect of the organophosphate structure on the physical and flame-retardant properties of an epoxy resin
    Shieh, JY
    Wang, CS
    JOURNAL OF POLYMER SCIENCE PART A-POLYMER CHEMISTRY, 2002, 40 (03) : 369 - 378
  • [36] A flame-retardant epoxy resin based on a reactive phosphorus-containing monomer of DODPP and its thermal and flame-retardant properties
    Gao, Li-Ping
    Wang, De-Yi
    Wang, Yu-Zhong
    Wang, Jun-Sheng
    Yang, Bing
    POLYMER DEGRADATION AND STABILITY, 2008, 93 (07) : 1308 - 1315
  • [37] Flame-retardant mechanism of silica: Effects of resin molecular weight
    Kashiwagi, T
    Shields, JR
    Harris, RH
    Davis, RD
    JOURNAL OF APPLIED POLYMER SCIENCE, 2003, 87 (09) : 1541 - 1553
  • [38] Flame-retardant mechanism of silica: Effects of resin molecular weight
    Kashiwagi, T. (takashi.kashiwagi@nist.gov), 1600, John Wiley and Sons Inc. (87):
  • [39] Preparation and flame retardancy of an intumescent flame-retardant epoxy resin system constructed by multiple flame-retardant compositions containing phosphorus and nitrogen heterocycle
    Yang, Shuang
    Wang, Jun
    Huo, Siqi
    Cheng, Liufeng
    Wang, Mei
    POLYMER DEGRADATION AND STABILITY, 2015, 119 : 251 - 259
  • [40] A FLAME RETARDANT EPOXY RESIN
    CASS, RA
    JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1961, 108 (03) : C56 - C56
12345