Hydration mechanism of a cementitious material prepared with Si-Mn slag

被引：0
|
作者：
Xu-fang Zhang1
机构：
来源：
InternationalJournalofMineralsMetallurgyandMaterials | 2011年 / 18卷 / 02期
关键词：
slag cement; mechanical properties; nuclear magnetic resonance (NMR); hydration;
D O I：
暂无
中图分类号：
TU578.1 [];
学科分类号：
摘要：
A cementitious material was prepared by mixing 80wt% Si-Mn slag powder, 10wt% lime, and 10wt% anhydrite. The compressive strength of mortar samples reaches 51.48 MPa after 28 d curing. The analyses of X-ray diffraction (XRD) and scanning electron microscopy (SEM) show that much ettringite is formed in the sample cured for 3 d, and C-S-H gel increases rapidly during subsequent curing. Nuclear magnetic resonance (NMR) analysis of 29Si and 27Al and infrared spectroscopy (IR) analysis show that aluminum decomposition from tetrahedral network of the slag glass and its subsequent migration and re-combination play an important role in the process of hydration and strength development of the samples.
引用
收藏
页码：234 / 239
页数：6
相关论文
共 50 条
  • [41] MECHANISM OF THE PIEZOELECTRIC RESISTANCE OF N-TYPE SI-MN SUBJECTED TO HYDROSTATIC COMPRESSION
    ABDURAIMOV, A
    ZAINABINIDOV, SZ
    TESHABAEV, A
    MAMATKARIMOV, OO
    KHIMMATKULOV, O
    SOVIET PHYSICS SEMICONDUCTORS-USSR, 1992, 26 (10): : 1036 - 1038
  • [42] Study on Cementitious Properties and Hydration Characteristics of Steel Slag
    Wang, Shuang
    Wang, Changlong
    Wang, Qunhui
    Liu, Zhenyu
    Qian, Wei
    Jin, ChangZhi
    Chen, Lie
    Li, Li
    POLISH JOURNAL OF ENVIRONMENTAL STUDIES, 2018, 27 (01): : 357 - 364
  • [43] Effects of Calcium Silicate Slag on Hydration of Cementitious Pastes
    Zhang, Ju
    Yan, Changwang
    Bai, Pucun
    Wang, Xiaoxiao
    Liu, Shuguang
    Liu, Zhigang
    MATERIALS, 2019, 12 (19)
  • [44] Hydration Reaction of Cementitious Composites with Calcium Silicate Slag
    Bai, Ru
    Zhang, Ju
    Yan, Changwang
    Liu, Shuguang
    Wang, Xiaoxiao
    Liu, Zhigang
    JOURNAL OF TESTING AND EVALUATION, 2023, 51 (06) : 4045 - 4057
  • [45] SI-MN EQUILIBRIUM IN FERROMANGANESE ALLOY PRODUCTION
    RANKIN, WJ
    SEE, JB
    TRANSACTIONS OF THE INSTITUTION OF MINING AND METALLURGY SECTION C-MINERAL PROCESSING AND EXTRACTIVE METALLURGY, 1980, 89 (JUN): : C91 - C92
  • [46] ANALYSIS OF DIFFUSION LAYERS IN SYSTEM SI-MN
    CEROVIC, D
    DJURIC, B
    MIKROCHIMICA ACTA, 1970, : 96 - &
  • [47] Hydration Characteristics and Mechanism of Partially Calcined Hydromagnesite – Calcined Clay Cementitious Material
    Liu Y.
    Qian X.
    Qin Y.
    Hu C.
    Wang F.
    Kuei Suan Jen Hsueh Pao/Journal of the Chinese Ceramic Society, 2023, 51 (08): : 1971 - 1978
  • [48] Properties and Hydration Mechanism of Ultrafine Magnesium Slag Powder-Cement Composites Cementitious Materials
    Sun R.
    Wu Z.
    Wang D.
    Ding Y.
    Fang K.
    Cailiao Daobao/Materials Reports, 2023, 37 (09):
  • [49] Hydration mechanism of alkali-activated cementitious materials entirely prepared by solid wastes
    Yang, Zhijie
    Tang, Wenhao
    Zhang, De
    Zhang, Jianming
    Wang, Kaiyue
    Zhao, Zhiming
    JOURNAL OF BUILDING ENGINEERING, 2024, 97
  • [50] Thermodynamics of Reducing Refining of Phosphorus from Si-Mn Alloy Using CaO-CaF2 Slag
    Shin, Jae Hong
    Park, Joo Hyun
    METALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE, 2012, 43 (06): : 1243 - 1246
12345