Hydration mechanism of a cementitious material prepared with Si-Mn slag

被引：0
|
作者：
Xu-fang Zhang1
机构：
来源：
InternationalJournalofMineralsMetallurgyandMaterials | 2011年 / 18卷 / 02期
关键词：
slag cement; mechanical properties; nuclear magnetic resonance (NMR); hydration;
D O I：
暂无
中图分类号：
TU578.1 [];
学科分类号：
摘要：
A cementitious material was prepared by mixing 80wt% Si-Mn slag powder, 10wt% lime, and 10wt% anhydrite. The compressive strength of mortar samples reaches 51.48 MPa after 28 d curing. The analyses of X-ray diffraction (XRD) and scanning electron microscopy (SEM) show that much ettringite is formed in the sample cured for 3 d, and C-S-H gel increases rapidly during subsequent curing. Nuclear magnetic resonance (NMR) analysis of 29Si and 27Al and infrared spectroscopy (IR) analysis show that aluminum decomposition from tetrahedral network of the slag glass and its subsequent migration and re-combination play an important role in the process of hydration and strength development of the samples.
引用
收藏
页码：234 / 239
页数：6
相关论文
共 50 条
  • [1] Hydration mechanism of a cementitious material prepared with Si-Mn slag
    Zhang, Xu-fang
    Ni, Wen
    Wu, Jun-yu
    Zhu, Li-ping
    INTERNATIONAL JOURNAL OF MINERALS METALLURGY AND MATERIALS, 2011, 18 (02) : 234 - 239
  • [2] Hydration mechanism of a cementitious material prepared with Si-Mn slag
    Zhang X.F.
    Ni W.
    Wu J.Y.
    Zhu L.P.
    International Journal of Minerals, Metallurgy, and Materials, 2011, 18 (2) : 234 - 239
  • [3] Experimental Research on Si-Mn Slag Cementitious Material
    Zhang, Xufang
    Wu, Junyu
    CIVIL ENGINEERING, ARCHITECTURE AND SUSTAINABLE INFRASTRUCTURE II, PTS 1 AND 2, 2013, 438-439 : 98 - +
  • [4] Synergistic Hydration Mechanism of Steel Slag-Slag Based Cementitious Material
    Nan X.
    Yang X.
    Zhang Y.
    Tang W.
    Zhang F.
    Jianzhu Cailiao Xuebao/Journal of Building Materials, 2024, 27 (04): : 366 - 374
  • [5] Research on hydration mechanism of slag composite cementitious material mixed with NaCl
    Liu, Chengbin
    Gao, Xiuqing
    Zhou, Yichao
    Journal of Chemical and Pharmaceutical Research, 2014, 6 (04) : 845 - 849
  • [6] Mechanical properties and hydration mechanism of Jinchuan nickel slag filling cementitious material
    Wen Z.-J.
    Gao Q.
    Yang Z.-Q.
    Yang X.-B.
    Ni W.
    Gao, Qian (gaoqian@ces.ustb.edu.cn), 1600, Central South University of Technology (31): : 1074 - 1083
  • [7] Ratio optimization and hydration mechanism of early strength cementitious material based on refining slag for mining
    Ruan Z.-E.
    Wu P.-J.
    Wu A.-X.
    Cao Y.-K.
    Wang S.-Y.
    Zhongguo Youse Jinshu Xuebao/Chinese Journal of Nonferrous Metals, 2023, 33 (09): : 3064 - 3076
  • [8] Physical Properties and Hydration of Cementitious Materials Prepared from Vanadium Slag and Phosphate Slag
    Pengyu Zhang
    Leming Ou
    Kun Liu
    Wentao Li
    Journal of Wuhan University of Technology-Mater. Sci. Ed., 2018, 33 : 1459 - 1464
  • [9] Physical Properties and Hydration of Cementitious Materials Prepared from Vanadium Slag and Phosphate Slag
    张鹏羽
    OU Leming
    刘琨
    LI Wentao
    JournalofWuhanUniversityofTechnology(MaterialsScience), 2018, 33 (06) : 1459 - 1464
  • [10] Physical Properties and Hydration of Cementitious Materials Prepared from Vanadium Slag and Phosphate Slag
    Zhang Pengyu
    Ou Leming
    Liu Kun
    Li Wentao
    JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION, 2018, 33 (06): : 1459 - 1464
12345