The low-temperature sintering and microwave dielectric properties of (Zn0.7Mg0.3)TiO3 ceramics with H3BO3

The effects of the addition of H 3 BO 3 on the microstructure, phase formation, and microwave dielectric properties of (Zn 0.7 Mg 0.3 )TiO 3 ceramics sintered at temperatures ranging from 890 ℃ to 950 ℃ are investigated. H 3 BO 3 as a sintering agent can effectively lower the sintering temperature of ZMT ceramics below 950 ℃ due to the liquid-phase effect. The microwave dielectric properties are found to strongly correlate with the amount of H 3 BO 3 . With the increase in H 3 BO 3 content, the dielectric constant (ε r ) monotonically increases, but the quality factor (Q × f ) reaches a maximum at 1 wt% H 3 BO 3 , and the apparent density of ZMT ceramics with H 3 BO 3 ≥ 1 wt% gradually decreases. At 950 ℃, the ZMT ceramics with 1% H 3 BO 3 exhibit excellent microwave dielectric properties: ε r = 19.8, and Q × f = 43800 GHz (8.94 GHz).