The Brittle Fracture Mechanism of Vanadium Alloy with High Level of Oxygen and Hydrogen

被引：0
|
作者：
CHEN Jiming XU Zengyu YANG Lin LIU Xiang
机构：
来源：
中国核科技报告 | 2002年 / 00期
关键词：
Vanadium alloy; Hydrogen embrittlement; Oxygen effect;
D O I：
暂无
中图分类号：
TL62 [聚变工程技术];
学科分类号：
082701 ;
摘要：
Hydrogen embrittlement is one of the key issues for the vanadium alloys for fusion application[1] . Previous study has shown that V4Ti alloy had better properties against the embrittlement than V4Cr4Ti and V4Ti3A1 alloys[2]. It was thought that
引用
收藏
页码：934 / 939
页数：6
相关论文
共 50 条
  • [31] MECHANISM OF FRACTURE OF GLASS AND SIMILAR BRITTLE SOLIDS
    TAYLOR, NW
    JOURNAL OF APPLIED PHYSICS, 1947, 18 (11) : 943 - 955
  • [32] FAILURE MECHANISM MODELS FOR BRITTLE-FRACTURE
    DASGUPTA, A
    HU, JM
    IEEE TRANSACTIONS ON RELIABILITY, 1992, 41 (03) : 328 - 335
  • [33] An analysis of the brittle fracture mechanism in cast steel
    Golaska, MB
    ECF 11 - MECHANISMS AND MECHANICS OF DAMAGE AND FAILURE, VOLS I-III, 1996, : 733 - 739
  • [34] DETERMINATION OF THE CRITICAL HYDROGEN CONCENTRATION FOR BRITTLE-FRACTURE OF A HIGH CHROMIUM FERRITIC STEEL
    YEN, SK
    SHIH, HC
    JOURNAL OF THE ELECTROCHEMICAL SOCIETY, 1990, 137 (07) : 2028 - 2031
  • [35] Research Progress on Hydrogen Separation Vanadium Alloy Membranes with High Flux and Hydrogen Embrittlement Resistance
    Meng, Ye
    Jiang, Peng
    Shi, Xiaobin
    Zhang, Shihong
    Song, Guangsheng
    Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering, 2021, 50 (03): : 1107 - 1112
  • [36] Research Progress on Hydrogen Separation Vanadium Alloy Membranes with High Flux and Hydrogen Embrittlement Resistance
    Meng Ye
    Jiang Peng
    Shi Xiaobin
    Zhang Shihong
    Song Guangsheng
    RARE METAL MATERIALS AND ENGINEERING, 2021, 50 (03) : 1107 - 1112
  • [37] Study on the brittle fracture of FeMoSiB nanocrystalline alloy ribbon
    Gan, Yang
    Zhou, Benlian
    Jinshu Xuebao/Acta Metallurgica Sinica, 2000, 36 (04): : 356 - 358
  • [38] Behaviour of vanadium and vanadium-iron alloy towards hydrogen
    Kirschfeld, L
    Sieverts, A
    ZEITSCHRIFT FUR ELEKTROCHEMIE UND ANGEWANDTE PHYSIKALISCHE CHEMIE, 1930, 36 : 123 - 129
  • [39] Research on Material Selection Method and Brittle Fracture Mechanism of High-Pressure Pipeline
    Li, Yulin
    Li, Zhihui
    SHOCK AND VIBRATION, 2023, 2023
  • [40] Kinetics of brittle fracture in metals under the influence of hydrogen
    Lepov, Valeriy
    Arkhanelskaja, Ekaterina
    Achikasova, Valentina
    1ST INTERNATIONAL CONFERENCE ON INTEGRITY AND LIFETIME IN EXTREME ENVIRONMENT (ILEE-2019), 2019, 20 : 24 - 29
12345