Annealing behavior of Al-Mg-Mn alloy processed by ECAP at elevated temperature

被引:0
|
作者
蒋大鸣 [1 ]
宁江利 [1 ]
孙俭峰 [2 ]
胡志敏 [3 ]
侯毅 [3 ]
机构
[1] School of Materials Science and Engineering,Harbin Institute of Technology
[2] School of Materials Science and Engineering,Heilongjiang Institute of Science and Technology  3. Northeast Light Alloy Co.Ltd.
关键词
Al-Mg-Mn alloy; equal channel angular pressing; annealing; EBSD;
D O I
暂无
中图分类号
TG166.3 [铝及其合金的热处理];
学科分类号
080201 ; 080503 ;
摘要
An Al-Mg-Mn alloy was subjected to equal channel angular pressing(ECAP)at 350℃for 6 passes.Static annealing was conducted on the deformed alloy at various temperatures from 400 to 450℃for 1h respectively.The microstructural evolutions of both the deformed and the annealed materials were studied by electron back scattering diffraction pattern(EBSD)analysis.A fine-grained structure with(sub)grain size of about 2μm is obtained after 6 ECAP passes,and the fraction of high-angle boundaries is 48.08%.As the annealing temperature increases,the average misorientations of the grain boundaries and the fraction of high-angle boundaries increases gradually.No grain growth takes place in the 400℃annealed sample,while after annealing at 450℃a coarse-grained structure replaces the initial fine-grained structure produced by ECAP.The aspect ratios remain almost constant and the(sub)grains keep equiaxed in the range of the present experiment.As the annealing temperature increases,the strength decreases obviously,which attributes to the relaxation of the internal stresses and the grain growth,while the elongation increases slightly.
引用
收藏
页码:248 / 254
页数:7
相关论文
共 50 条
  • [31] Aging behavior of ECAP processed AZ80 Mg alloy
    Ogushi, Yoshifumi
    Mostaed, Ehsan
    Dellasega, David
    Vedani, Maurizio
    Miyamoto, Hiroyuki
    Fujiwara, Hiroshi
    6TH INTERNATIONAL CONFERENCE ON NANOMATERIALS BY SEVERE PLASTIC DEFORMATION (NANOSPD6), 2014, 63
  • [32] Al-Mg-Mn焊丝合金
    范爱国
    兵器材料科学与工程, 2008, (01) : 42 - 42
  • [33] Microstructure, hardness evolution and thermal stability of binary Al-7Mg alloy processed by ECAP with intermediate annealing
    Zha, Min
    Li, Yan-jun
    Mathiesen, Ragnvald
    Bjorge, Ruben
    Roven, Hans J.
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2014, 24 (07) : 2301 - 2306
  • [34] Microstructure, mechanical behavior and low temperature superplasticity of ECAP processed ZM21 Mg alloy
    Mostaed, Ehsan
    Fabrizi, Alberto
    Dellasega, David
    Bonollo, Franco
    Vedani, Maurizio
    JOURNAL OF ALLOYS AND COMPOUNDS, 2015, 638 : 267 - 276
  • [35] Microstructure, mechanical behavior and low temperature superplasticity of ECAP processed ZM21 Mg alloy
    Mostaed, Ehsan
    Fabrizi, Alberto
    Dellasega, David
    Bonollo, Franco
    Vedani, Maurizio
    Journal of Alloys and Compounds, 2015, 638 : 267 - 276
  • [36] Deformation behavior of Al-Mg-Si alloy at the elevated temperature
    Kwon, Y.-N.
    Lee, Y. S.
    Lee, J. H.
    JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2007, 187 : 533 - 536
  • [37] Fracture behavior of Al-Mg alloy in elevated temperature processes
    Wang, PT
    Roadman, RE
    Jin, Z
    Alexandrov, S
    HOT DEFORMATION OF ALUMINUM ALLOYS III, 2003, : 483 - 497
  • [38] Superior combined strength and elongation by conducting elevated temperature constrained groove pressing on Al-Mg-Mn sheets
    Jebelli, A. Ahmadi
    Fereshteh-Saniee, F.
    MATERIALS CHEMISTRY AND PHYSICS, 2023, 307
  • [39] Superplastic behaviour of the Al-Mg-Sc-Zr alloy processed by ECAP
    Málek, P
    Cieslar, M
    Bartuska, P
    Drbohlav, I
    KOVOVE MATERIALY-METALLIC MATERIALS, 2005, 43 (04): : 245 - 257
  • [40] The influence of specimens geometry on the PLC effect in Al-Mg-Mn (5182) alloy
    Zdunek, J.
    Spychalski, W. L.
    Mizera, J.
    Kurzydlowski, K. J.
    MATERIALS CHARACTERIZATION, 2007, 58 (01) : 46 - 50