Morphologies and corrosion resistances of electroless Ni-P coated nanoporous coppers

被引：0
|
作者：
YANG Qing [1 ,2 ]
LIANG ShuHua [1 ,2 ]
WANG Jia [1 ]
WANG Ying [1 ]
机构：
[1] Faculty of Material Science and Engineering,Xi'an University of Technology
[2] Shaanxi Province Key Laboratory for Electrical Materials and Infiltration Technology
来源：
Science China(Technological Sciences) | 2013年 / 05期
基金：
中国国家自然科学基金;
关键词：
nanoporous copper; morphology; corrosion resistance; Ni-P coating; electroless plating; complexing agent;
D O I：
暂无
中图分类号：
TB304 [材料腐蚀与保护];
学科分类号：
摘要：
In order to improve the corrosion resistance of nanoporous coppers(NPCs),the electroless Ni-P coated NPCs were prepared in plating solutions with different pH values(5,8,11) and complexing agent(actic acid,citric acid).The morphologies and corrosion resistances of the as-prepared samples were investigated.The results showed that the double complexing agent composed of lactic acid and citric acid is relatively suitable for preparing the Ni-P coated NPC with three-dimensional continuous interpenetrating ligament-channel structures,and the uniform ligaments and nanoporous channels could be obtained at pH8.The Ni-P coated NPC showed higher corrosion potentials than NPC in H2SO4,NaOH and NaCl corrosion solutions.
引用
收藏
页码：1147 / 1150
页数：4
相关论文
共 50 条
  • [11] Characterisation of electroless Ni-P and electroless composite coatings Ni-P/Ni-PTFE
    Karaguiozova, Zdravka K.
    INTERNATIONAL JOURNAL OF SURFACE SCIENCE AND ENGINEERING, 2018, 12 (5-6) : 496 - 506
  • [12] Study on morphology and corrosion resistance of electroless Ni-P coatings
    Rahimi, A. R.
    Modarres, H.
    Abdouss, M.
    SURFACE ENGINEERING, 2009, 25 (05) : 367 - 371
  • [13] Corrosion Characteristics of Electroless Ni-P Coating in Naphthenic Acid
    Chen, Zhiliang
    Lin, An
    Gan, Fuxing
    Fang, Dajing
    Hao, Long
    Zhang, Yeming
    MATERIALS PERFORMANCE, 2009, 48 (04) : 38 - 42
  • [14] An optical fibre corrosion sensor with an electroless deposit of Ni-P
    Abderrahmane, S
    Himour, A
    Kherrat, R
    Chailleux, E
    Jaffrezic-Renault, N
    Stremsdoerfer, G
    SENSORS AND ACTUATORS B-CHEMICAL, 2001, 75 (1-2) : 1 - 4
  • [15] Corrosion characteristics of electroless Ni-P coating in naphthenic acid
    Department of Environmental Engineering, Wuhan, China
    不详
    不详
    Mater Perform, 2009, 4 (38-42):
  • [16] Evaluation of the corrosion resistance of electroless Ni-P coatings on magnesium
    Ramirez, Laura Quiroz
    Amador, Anderson Sandoval
    Echeverria, Felix Echeverria
    Castano Gonzalez, Juan Guillermo
    Pena Ballesteros, Dario Yesid
    MATERIA-RIO DE JANEIRO, 2020, 25 (04): : 1 - 8
  • [17] Electroless deposited Ni-P alloys: corrosion resistance mechanism
    Elsener, Bernhard
    Crobu, Maura
    Scorciapino, Mariano Andrea
    Rossi, Antonella
    JOURNAL OF APPLIED ELECTROCHEMISTRY, 2008, 38 (07) : 1053 - 1060
  • [18] The effect of electroless Ni-P interlayer on corrosion behavior of TiN-coated austempered ductile iron
    Hsu, Cheng-Hsun
    Huang, Kuan-Hao
    Chen, Yi-Tsung
    Ho, Wei-Yu
    THIN SOLID FILMS, 2013, 529 : 34 - 38
  • [19] CORROSION PROTECTION OF TIN-COATED LOW-CARBON STEEL WITH ELECTROLESS NI-P AS AN INTERLAYER
    HE, JL
    HON, MH
    SURFACE & COATINGS TECHNOLOGY, 1992, 53 (01): : 93 - 98
  • [20] Preparation and properties of electroless Ni-P coated barium ferrite powders
    Wu, Xiao-Wei
    Feng, Yu-Jie
    Liu, Yan-Kun
    Wei, Han
    Harbin Gongye Daxue Xuebao/Journal of Harbin Institute of Technology, 2010, 42 (04): : 584 - 587
12345