Fractal Dimensions of Hydrogen Induced Brittle Fracture of Titanium Aluminide

被引：0
|
作者：
Yue ZHANG Yanbin WANG Lijie QIAO Wuyang CHU Chimei HSIAO Dept.of Materials Physics
机构：
来源：
Journal of Materials Science & Technology | 1993年 / 05期
关键词：
titanium aluminide; hydrogen induced cracking; tractal dimension;
D O I：
暂无
中图分类号：
学科分类号：
摘要：
The relationship between the stress intensity factor K;required for brittle crack initiation and propa-gation and the fractal dimension D;of the fracture surface was derived,i.e,InK;=（1/2）In2γE’+（1/2）In（d;/L;）(1-D;)The real surface energy can be calculated based on the measured linear relation of the InK;vs D;,The equation is not only suitable for the overload fracture but also for the delayed fracture,e.g.hydrogen induced cracking （HIC） and stress corrosion cracking （SCC）.The experiment resultsshowed that the hydrogen induced delayed cracking occurred in the Ti-24AI-11 Nb alloy during dy-namic charging,and the threshold stress intensity factor was very low,i.e..K;/K;= 0.43.The ex-perimental relationship between the stress intensity factor K;and D;was consistent with the theo-retical equation.
引用
下载
收藏
页码：338 / 342
页数：5
相关论文
共 50 条
  • [21] BRITTLE-FRACTURE OF FRACTAL CUBIC AGGREGATES
    PERFECT, E
    KAY, BD
    SOIL SCIENCE SOCIETY OF AMERICA JOURNAL, 1995, 59 (04) : 969 - 974
  • [22] On the fractal fracture in brittle structures numerical approach
    Panagouli, OK
    Mistakidis, ES
    Panagiotopoulos, PD
    COMPUTER METHODS IN APPLIED MECHANICS AND ENGINEERING, 1997, 147 (1-2) : 1 - 15
  • [23] BRITTLE FRACTURE IN ALPHA-TITANIUM
    AMATEAU, MF
    BURRIER, HI
    EBERT, LJ
    ASM TRANSACTIONS QUARTERLY, 1966, 59 (04): : 920 - &
  • [24] Hydrogen solubility in a titanium aluminide alloy - Comment
    Thompson, AW
    Chu, WY
    Williams, JC
    SCRIPTA MATERIALIA, 1996, 35 (10) : 1195 - 1198
  • [25] Hydrogen enhanced thermal fatigue of γ-titanium aluminide
    Dunfee, William, 1600, Pergamon Press Inc, Tarrytown, NY, United States (33):
  • [26] Hydrogen effects and microstructure in titanium aluminide alloys
    Thompson, AW
    PROCESSING AND DESIGN ISSUES IN HIGH TEMPERATURE MATERIALS, 1996, : 319 - 330
  • [27] Effect of hydrogen on cathodic corrosion of titanium aluminide
    Gao, KW
    Jin, JW
    Qiao, LJ
    Chu, WY
    Hsiao, CM
    CORROSION, 1996, 52 (01) : 3 - 7
  • [28] Compressive Fracture of Brittle Geomaterial: Fractal Features of Compression-Induced Fracture Surfaces and Failure Mechanism
    Ren, L.
    Xie, L. Z.
    Li, C. B.
    Wang, J.
    ADVANCES IN MATERIALS SCIENCE AND ENGINEERING, 2014, 2014
  • [29] Establishing a protocol for measurements of fractal dimensions in brittle materials
    Hill, TJ
    Della Bona, A
    Mecholsky, JJ
    JOURNAL OF MATERIALS SCIENCE, 2001, 36 (11) : 2651 - 2657
  • [30] Establishing a protocol for measurements of fractal dimensions in brittle materials
    T. J. Hill
    A. Della Bona
    J. J. Mecholsky
    Journal of Materials Science, 2001, 36 : 2651 - 2657
12345