Fatigue test of carbon epoxy composite high pressure hydrogen storage vessel under hydrogen environment

被引：0
|
作者：
Chuan-xiang ZHENG [1 ]
Liang WANG [1 ]
Rong LI [1 ]
Zong-xin WEI [1 ]
Wei-wei ZHOU [1 ]
机构：
[1] Institute of Chemical Machinery and Process Equipment, Zhejiang University
来源：
Journal of Zhejiang University-Science A(Applied Physics & Engineering) | 2013年 / 06期
关键词：
Hydrogen storage vessel; Composite; Fatigue test; High pressure; Temperature raise;
D O I：
暂无
中图分类号：
U465.6 [复合材料]; TB33 [复合材料];
学科分类号：
摘要：
A significant temperature raise within hydrogen vehicle cylinder during the fast filling process will be observed, while the strength and fatigue life of the cylinder will dramatically decrease at high temperature. In order to evaluate the strength and fatigue of composite hydrogen storage vessel, a 70-MPa fatigue test system using hydrogen medium was set up. Experimental study on the fatigue of composite hydrogen storage vessels under real hydrogen environment was performed. The experimental results show that the ultimate strength and fatigue life both decreased obviously compared with the values under hydraulic fatigue test. Furthermore, fatigue property, failure behavior, and safe hydrogen charging/discharging working mode of onboard hydrogen storage vessels were obtained through the fatigue tests.
引用
收藏
页码：393 / 400
页数：8
相关论文
共 50 条
  • [41] Surface coating with a high resistance to hydrogen entry under high-pressure hydrogen-gas environment
    Yamabe, Junichiro
    Matsuoka, Saburo
    Murakami, Yukitaka
    INTERNATIONAL JOURNAL OF HYDROGEN ENERGY, 2013, 38 (24) : 10141 - 10154
  • [42] Nickel-hydrogen single pressure vessel storage battery
    Matryonin, VI
    Bazhenov, MD
    Gromov, VV
    Kondratyev, DG
    Popov, VN
    Soloviov, GS
    Stikhin, AS
    Schipanov, IV
    HYDROGEN ENERGY PROGRESS XIII, VOLS 1 AND 2, PROCEEDINGS, 2000, : 883 - 886
  • [43] Effects of hydrogen pressure, test frequency and test temperature on fatigue crack growth properties of low-carbon steel in gaseous hydrogen
    Yamabe, Junichiro
    Yoshikawa, Michio
    Matsunaga, Hisao
    Matsuoka, Saburo
    21ST EUROPEAN CONFERENCE ON FRACTURE, (ECF21), 2016, 2 : 525 - 532
  • [44] OVERVIEW OF STANDARDS ON PRESSURE CYCLING TEST FOR ON-BOARD COMPOSITE HYDROGEN STORAGE CYLINDERS
    Huang, Qianghua
    Li, Xiang
    Li, Jiepu
    Liu, Yitao
    Li, Xin
    Zhu, Chaoyang
    PROCEEDINGS OF ASME 2022 PRESSURE VESSELS AND PIPING CONFERENCE, PVP2022, VOL 1, 2022,
  • [45] Study of composite polymer degradation for high pressure hydrogen vessel by machine learning approach
    Kadri, K.
    Kallel, A.
    Guerard, G.
    Ben Abdallah, A.
    Ballut, S.
    Fitoussi, J.
    Shirinbayan, M.
    ENERGY STORAGE, 2024, 6 (04)
  • [46] Analysis of the cost-effectiveness of pressure for vehicular high-pressure gaseous hydrogen storage vessel
    Sun, Bai-gang
    Zhang, Dong-sheng
    Liu, Fu-shui
    INTERNATIONAL JOURNAL OF HYDROGEN ENERGY, 2012, 37 (17) : 13088 - 13091
  • [47] Hydrogen storage properties of nanostructured MgH2/TiH2 composite prepared by ball milling under high hydrogen pressure
    Shao, H.
    Felderhoff, M.
    Schueth, F.
    INTERNATIONAL JOURNAL OF HYDROGEN ENERGY, 2011, 36 (17) : 10828 - 10833
  • [48] Steel-Concrete Composite Pressure Vessels for Hydrogen Storage at High Pressures
    Jawad, Maan
    Wang, Yanli
    Feng, Zhili
    JOURNAL OF PRESSURE VESSEL TECHNOLOGY-TRANSACTIONS OF THE ASME, 2020, 142 (02):
  • [49] Damage in Thermoplastic Composite Structures: Application to High Pressure Hydrogen Storage Vessels
    Thomas, C.
    Nony, F.
    Villalonga, S.
    Renard, J.
    FATIGUE BEHAVIOUR OF FIBER REINFORCED POLYMERS: EXPERIMENTS AND SIMULATIONS, 2012, : 33 - 47
  • [50] Failure pressure analysis of hydrogen storage pipeline under low temperature and high pressure
    Chen, Zhanfeng
    Chen, Yipeng
    Wang, Wen
    Lu, Keqing
    Yang, He
    Zhu, Weiping
    INTERNATIONAL JOURNAL OF HYDROGEN ENERGY, 2020, 45 (43) : 23142 - 23150
12345