Multilayer Clad Plate of Stainless Steel/Aluminum/ Aluminum Alloy

被引：0
|
作者：
袁家伟 [1 ]
庞玉华 [1 ]
机构：
[1] School of Metallurgy Engineering, Xi’an University of Architecture & Technology
来源：
Journal of Wuhan University of Technology(Materials Science) | 2011年 / 01期
关键词：
multilayer clad plate; hot rolling; bonding strength; stretch strength;
D O I：
暂无
中图分类号：
TG146.21 [];
学科分类号：
080502 ;
摘要：
The 3, 5, 20 layer clad plate from austenitic stainless steel, pure aluminum and aluminum alloy sheets were fabricated in different ways. The stretch and interface properties were measured. The result shows that 20 layer clad plate is better than the others. Well-bonded clad plate was successfully obtained in the following procedure: Basic clad sheet from 18 layer Al1060/Al3003 sheets was firstly obtained with an initial rolling reduction of 44% at 450 ℃, followed by annealing at 300 ℃, and then with reduction of 50% at 550 ℃ from STS304 on each side. The best 20 layer clad plate was of 129 MPa bonding strength and 225 MPa stretch strength.
引用
收藏
页码：111 / 113
页数：3
相关论文
共 50 条
  • [1] Multilayer Clad Plate of Stainless Steel/Aluminum/Aluminum Alloy
    Yuan Jiawei
    Pang Yuhua
    Li Ting
    JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION, 2011, 26 (01): : 111 - 113
  • [2] Multilayer clad plate of stainless steel/aluminum/aluminum alloy
    Jiawei Yuan
    Yuhua Pang
    Ting Li
    Journal of Wuhan University of Technology-Mater. Sci. Ed., 2011, 26 : 111 - 113
  • [3] Processing 20 Ply Clad Plate by Accumulative Clad Rolling from Stainless Steel/Aluminum/Aluminum Alloy.../Stainless Steel Sheets
    Pang, Yuhua
    Yuan, Jiawei
    Sun, Qi
    Hu, Yanglei
    MATERIALS RESEARCH, PTS 1 AND 2, 2009, 610-613 : 454 - 458
  • [4] Explosive welding conditions and their bonding strength in various aluminum alloy and stainless steel clad using stainless steel intermediate plate
    Hokamoto, Kazuyuki
    Izuma, Takeshi
    Andoh, Takenobu
    Fujita, Masahiro
    Yosetsu Gakkai Ronbunshu/Quarterly Journal of the Japan Welding Society, 1993, 11 (01): : 16 - 21
  • [5] Ultrasonic butt welding of aluminum, aluminum alloy and stainless steel plate specimens
    Tsujino, J
    Hidai, K
    Hasegawa, A
    Kanai, R
    Matsuura, H
    Matsushima, K
    Ueoka, T
    ULTRASONICS, 2002, 40 (1-8) : 371 - 374
  • [6] Forming limit diagram of stainless steel-aluminum alloy clad
    Liu Hong-wei
    Zhang Peng
    NEW MATERIALS AND ADVANCED MATERIALS, PTS 1 AND 2, 2011, 152-153 : 541 - 544
  • [7] Calculations of Stainless Steel-Aluminum Alloy Clad Forming Limit
    Liu, Hongwei
    Zhang, Peng
    ADVANCED RESEARCH ON ELECTRONIC COMMERCE, WEB APPLICATION, AND COMMUNICATION, PT 2, 2011, 144 : 285 - 290
  • [8] Analysis of tension property of stainless steel-aluminum alloy clad
    Liu, Hongwei
    Guo, Cheng
    Zang, Shunlai
    Zhongguo Jixie Gongcheng/China Mechanical Engineering, 2007, 18 (07): : 862 - 865
  • [9] Study on the characteristic of stainless steel clad aluminum composite
    Zhu, Xuxia
    Yuan, Gecheng
    Li, Zuojian
    Peng, Dashu
    Zhu, Zhaohua
    Yin, Deyan
    Zhou, Jingmin
    Liang, Huidong
    Rejiagong Gongyi/Hot Working Technology, 2000, (01): : 38 - 40
  • [10] Anisotropic Properties of Stainless Steel - Clad Aluminum Sheet
    Kim, Daeyong
    Hwang, Bum Kyu
    Lee, Young Seon
    Kim, Ji Hoon
    Kim, Min-Joong
    NUMIFORM 2010, VOLS 1 AND 2: DEDICATED TO PROFESSOR O. C. ZIENKIEWICZ (1921-2009), 2010, 1252 : 357 - +
12345