Fabrication of Ti2AlC by Spark Plasma Sintering from Elemental Powders and Thermodynamics Analysis of Ti-Al-C System

被引：0
|
作者：
王苹
机构：
[1] Wuhan 430070
[2] China School of Sciences
[3] State Key Laboratory of Advanced Technology for Materials Synthesis and Processing Wuhan University of Technology
来源：
Journal of Wuhan University of Technology(Materials Science Edition) | 2007年 / 02期
基金：
中国国家自然科学基金;
关键词：
Ti2; AlC; spark plasma sintering; elemental powder; thermodynamics analysis;
D O I：
暂无
中图分类号：
O614.411 [];
学科分类号：
摘要：
A ternary-layered carbide Ti 2 AlC material could be synthesized by spark plasma sintering(SPS)technology using elemental powder mixture of Ti,Al and active carbon.By means of XRD and SEM,phases were identified and microscopically evaluated.The experimental results show that the main phase in the product was fully crystallized Ti 2 AlC with small particle size when sintered at 1200 C.The syn-thesis temperature of SPS was 200-400 C lower than that of hot pressing(HP)or hot isostatic pressing(HIP). Through thermodynamics calculations,the mechanism of Ti 2 AlC was studied by calculating changes of Gibbs free energy of reactions.
引用
收藏
页码：325 / 328
页数：4
相关论文
共 50 条
  • [41] Synthesis of Ti3SiC2 by spark plasma sintering(SPS) of elemental powders
    朱教群
    梅炳初
    何利萍
    陈艳林
    TransactionsofNonferrousMetalsSocietyofChina, 2003, (01) : 46 - 49
  • [42] Investigation on the in-situ reaction mechanism of Ti2AlC/TiAl composite prepared by spark plasma sintering
    Wang, Zhenbo
    Liu, Pei
    Hou, Bo
    Ye, Feng
    Wang, Aiqin
    Xie, Jingpei
    MATERIALS CHARACTERIZATION, 2022, 194
  • [43] Dilatometric sintering of Ti-2Al and Ti-5Al elemental powders
    Panigrahi, Bharat B.
    Reddy, N. Subba
    Das, Karabi
    Godkhindi, M. M.
    JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY, 2007, 23 (03) : 363 - 366
  • [44] Transforming the amorphous Ti-Al-C coatings to high-purity Ti2AlC MAX phase coatings by prolonged annealing at 550 °C
    Wang, Zhenyu
    Li, Wentao
    Wang, Cuicui
    Wu, Haichen
    Ke, Peiling
    Wang, Aiying
    MATERIALS LETTERS, 2020, 261 (261)
  • [45] Synthesis of high pure Ti3AlC2 and Ti2AlC powders from TiH2 powders as Ti source by tube furnace
    Li Liang
    Zhou Aiguo
    Xu Lin
    Li Zhengyang
    Wang Libo
    JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION, 2013, 28 (05): : 882 - 887
  • [46] Synthesis of High Pure Ti3AlC2 and Ti2AlC Powders from TiH2 Powders as Ti Source by Tube Furnace
    李良
    周爱国
    XU Lin
    LI Zhengyang
    WANG Libo
    Journal of Wuhan University of Technology(Materials Science), 2013, (05) : 882 - 887
  • [47] Synthesis of high pure Ti3AlC2 and Ti2AlC powders from TiH2 powders as Ti source by tube furnace
    Liang Li
    Aiguo Zhou
    Lin Xu
    Zhengyang Li
    Libo Wang
    Journal of Wuhan University of Technology-Mater. Sci. Ed., 2013, 28 : 882 - 887
  • [48] Fabrication of textured Ti3AlC2 by spark plasma sintering and their anisotropic mechanical properties
    Mizuno, Yutaka
    Sato, Kimitoshi
    Mrinalini, Mishra
    Suzuki, Tohru S.
    Sakka, Yoshio
    JOURNAL OF THE CERAMIC SOCIETY OF JAPAN, 2013, 121 (1412) : 366 - 369
  • [49] Synthesis of Cr2AlC from Elemental Powders with Modified Pressureless Spark Plasma Sintering
    葛梦妮
    WANG Xiaofan
    LI Gaiye
    LU Chen
    张建峰
    TU Rong
    JournalofWuhanUniversityofTechnology(MaterialsScience), 2019, 34 (02) : 287 - 292
  • [50] Synthesis of Cr2AlC from Elemental Powders with Modified Pressureless Spark Plasma Sintering
    Ge Mengni
    Wang Xiaofan
    Li Gaiye
    Lu Chen
    Zhang Jianfeng
    Tu Rong
    JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION, 2019, 34 (02): : 287 - 292
12345