Microstructures and mechanical properties of high strength Mg-Zn-Mn alloy

被引：11
|
作者：
张丁非 [1 ,2 ]
石国梁 [2 ]
戴庆伟 [2 ]
袁炜 [2 ]
段红玲 [2 ]
机构：
[1] National Engineering Research Center for Magnesium Alloys,Chongqing University
[2] College of Materials Science and Engineering,Chongqing University
来源：
TransactionsofNonferrousMetalsSocietyofChina | 2008年 / 18(S1)卷 / S1期
关键词：
high strength; Mg-Zn-Mn alloy; microstructures; mechanical properties;
D O I：
暂无
中图分类号：
TG146.22 [];
学科分类号：
080502 ;
摘要：
The microstructures and mechanical properties of a new Mg-6%Zn-1%Mn(mass fraction) wrought magnesium alloy were studied,which could be extruded smoothly at 310-330℃with a complete dynamic recrystallization.After solution treatment one and two-step aging techniques were used.All as-aged microstructures contained two types of dispersed phases:β’ phases and pureα-Mn particles.The two-step aging had a better strengthening effect than the traditional one-step aging,and the strength value achieved by the two-step aging could reach that of the ZK60 wrought magnesium alloy.The outstanding precipitation strengthening effect of the alloy should be attribute to the GP zones,diffusive solute-rich zones and some metastable phases formed during the first step aging that provide more effective nuclei for Mg-Zn strengthening phases during the second step aging.
引用
收藏
页码：59 / 63
页数：5
相关论文
共 50 条
  • [41] Effect of solution treatments on the microstructures and mechanical properties of Mg-2Zn-0.8Mn-0.5Ca alloy
    Du, Hui
    Wei, Zunjie
    MANUFACTURING SCIENCE AND ENGINEERING, PTS 1-5, 2010, 97-101 : 2237 - 2240
  • [42] Effects of quench rate on mechanical properties and microstructures of high strength and toughness Al-Zn-Mg-Cu alloy with Sc(Zr) addition
    Li F.-F.
    Xu G.-F.
    Li Y.
    Huang J.-W.
    Deng Y.
    Yin Z.-M.
    Huang, Ji-Wu (huangjiwu_CSU@163.com), 1600, Central South University of Technology (30): : 264 - 272
  • [43] Microstructures and mechanical properties of high-strength Mg-Gd-Y-Zn-Zr alloy sheets processed by severe hot rolling
    Xu, C.
    Xu, S. W.
    Zheng, M. Y.
    Wu, K.
    Wang, E. D.
    Kamado, S.
    Wang, G. J.
    Lv, X. Y.
    JOURNAL OF ALLOYS AND COMPOUNDS, 2012, 524 : 46 - 52
  • [44] Microstructure and properties of Al-Zn-Mg-Cu-Mn in-situ high strength alloy
    Cai, YuanHua
    Cui, Hua
    Li, YongBing
    Hang, JingFeng
    Zhang, JiShan
    PRICM 6: SIXTH PACIFIC RIM INTERNATIONAL CONFERENCE ON ADVANCED MATERIALS AND PROCESSING, PTS 1-3, 2007, 561-565 : 957 - +
  • [45] Researches on microstructures and mechanical properties of extruded Mg-Zn-Zr-Y alloy
    Peng, Jian
    Liu, Rongshen
    Zhang, Dingfei
    Song, Chengmeng
    PROGRESSES IN FRACTURE AND STRENGTH OF MATERIALS AND STRUCTURES, 1-4, 2007, 353-358 : 715 - 717
  • [46] Effect of Ce on microstructures and mechanical properties of rapidly solidified Mg-Zn alloy
    Zhou, T.
    Xia, H.
    Chen, Z. H.
    MATERIALS SCIENCE AND TECHNOLOGY, 2011, 27 (07) : 1198 - 1205
  • [47] Microstructures and Mechanical Properties of a Novel Mg-Gd-Y-Zn-Zr Alloy
    Yang, Zhong
    Li, Jianping
    Wang, Yanrong
    Xiong, Biwei
    LIGHT METALS TECHNOLOGY 2013, 2013, 765 : 521 - +
  • [48] Zn-Mn-Mg alloy with superior mechanical properties and antibacterial performance
    Tang, Yubo
    Huang, Sheng
    Chen, Wei-chih
    Garu, A.
    Linghu, Xitao
    Wa, Qingde
    Huang, Shuai
    Chen, Jian
    ADVANCED COMPOSITES AND HYBRID MATERIALS, 2025, 8 (01)
  • [49] Mechanical properties of naturally aged Mg-Zn-Cu-Mn alloy
    Buha, J.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2008, 489 (1-2): : 127 - 137
  • [50] Microstructural and constitutive analysis in process modeling of hot working: The case of a Mg-Zn-Mn alloy
    Spigarelli, S.
    Jager, A.
    El Mehtedi, M.
    Gartnerova, V.
    MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING, 2016, 661 : 40 - 50
12345