Microstructures and mechanical properties of high strength Mg-Zn-Mn alloy

被引：11
|
作者：
张丁非 [1 ,2 ]
石国梁 [2 ]
戴庆伟 [2 ]
袁炜 [2 ]
段红玲 [2 ]
机构：
[1] National Engineering Research Center for Magnesium Alloys,Chongqing University
[2] College of Materials Science and Engineering,Chongqing University
来源：
TransactionsofNonferrousMetalsSocietyofChina | 2008年 / 18(S1)卷 / S1期
关键词：
high strength; Mg-Zn-Mn alloy; microstructures; mechanical properties;
D O I：
暂无
中图分类号：
TG146.22 [];
学科分类号：
080502 ;
摘要：
The microstructures and mechanical properties of a new Mg-6%Zn-1%Mn(mass fraction) wrought magnesium alloy were studied,which could be extruded smoothly at 310-330℃with a complete dynamic recrystallization.After solution treatment one and two-step aging techniques were used.All as-aged microstructures contained two types of dispersed phases:β’ phases and pureα-Mn particles.The two-step aging had a better strengthening effect than the traditional one-step aging,and the strength value achieved by the two-step aging could reach that of the ZK60 wrought magnesium alloy.The outstanding precipitation strengthening effect of the alloy should be attribute to the GP zones,diffusive solute-rich zones and some metastable phases formed during the first step aging that provide more effective nuclei for Mg-Zn strengthening phases during the second step aging.
引用
收藏
页码：59 / 63
页数：5
相关论文
共 50 条
  • [1] Microstructures and mechanical properties of high strength Mg-Zn-Mn alloy
    Zhang Ding-fei
    Shi Guo-liang
    Dai Qing-wei
    Yuan Wei
    Duan Hong-ling
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2008, 18 : S59 - S63
  • [2] Effect of Y addition on microstructure and mechanical properties of Mg-Zn-Mn alloy
    Qi, Fu-gang
    Zhang, Ding-fei
    Zhang, Xiao-hua
    Pan, Fu-sheng
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2014, 24 (05) : 1352 - 1364
  • [3] Researches on extrusion, microstructure and mechanical properties of new Mg-Zn-Mn alloy
    College of Materials Science and Engineering, Chongqing University, Chongqing 400045, China
    不详
    Cailiao Gongcheng, 2008, 4 (38-42):
  • [4] Deformation microstructures and texture evolution of the Mg-Zn-Mn alloy with high strain rate rolling
    Wu, Qin
    Fan, Caihe
    Yan, Hongge
    Yang, Jianjun
    Zheng, Dongsheng
    Ou, Ling
    Hu, Zeyi
    Ni, Yumeng
    JOURNAL OF MATERIALS RESEARCH, 2023, 38 (02) : 404 - 415
  • [5] Effect of Ca on the Microstructure, Texture and Mechanical Properties in Mg-Zn-Mn Based Alloy
    Suh, Byeong-Chan
    Sasaki, Taisuke
    Nakata, Taiki
    Kamado, Shigeharu
    Hono, Kazuhiro
    MAGNESIUM TECHNOLOGY 2017, 2017, : 525 - 531
  • [6] Effects of Zn Content and Heat Treatment on Microstructures and Mechanical Properties of Mg-Zn-Mn Wrought Magnesium Alloys
    Zhang Dingfei
    Zhao Xiabing
    Shi Guoliang
    Qi Fugang
    RARE METAL MATERIALS AND ENGINEERING, 2011, 40 (03) : 418 - 423
  • [7] Effect of Zn on mechanical property and corrosion property of extruded Mg-Zn-Mn alloy
    尹冬松
    张二林
    曾松岩
    TransactionsofNonferrousMetalsSocietyofChina, 2008, (04) : 763 - 768
  • [8] Effect of Zn on mechanical property and corrosion property of extruded Mg-Zn-Mn alloy
    Yin Dong-song
    Zhang Er-lin
    Zeng Song-yan
    TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2008, 18 (04) : 763 - 768
  • [9] Effects of Mn Content on Microstructure and Mechanical Properties of Mg-Zn-Mn Wrought Alloys
    Zhang Dingfei
    Qi Fugang
    Shi Guoliang
    Dai Qingwei
    RARE METAL MATERIALS AND ENGINEERING, 2010, 39 (12) : 2205 - 2210
  • [10] Microstructures and mechanical properties of high-strength Mg-Gd-Y-Zn-Zr alloy
    Wang, Zhen-Dong
    Fang, Can-Feng
    Meng, Ling-Gang
    Li, Nai-Pu
    Wu, You-Fang
    Zhang, Xing-Guo
    Zhongguo Youse Jinshu Xuebao/Chinese Journal of Nonferrous Metals, 2012, 22 (01): : 1 - 6
12345