Effect of post-weld heat treatment on microstructure and properties of Ti-23Al-17Nb alloy laser beam welding joints

被引：1
|
作者：
王国庆 [1 ]
吴爱萍 [1 ]
赵玥 [1 ]
邹贵生 [1 ]
陈强 [1 ]
任家烈 [1 ]
机构：
[1] Key Laboratory for Advanced Materials Processing Technology of the Ministry of Education,Department of Mechanical Engineering,Tsinghua University
来源：
Transactions of Nonferrous Metals Society of China | 2010年 / 20卷 / 05期
关键词：
Ti-23Al-17Nb; Ti3Al-based alloy; laser beam welding; post-weld heat treatment; mechanical properties;
D O I：
暂无
中图分类号：
TG456.7 [激光焊];
学科分类号：
080201 ; 080503 ;
摘要：
The mechanical properties of Ti-23Al-17Nb (mole fraction,%) laser beam welding alloy joint at room temperature are comparable to that of the base materials.However,the strength and ductility of the as-welded joint deteriorate seriously after high temperature circulation.The effect of post-welded heat treatment on the microstructure and mechanical properties of the joint was investigated.The heat treatment was taken at 980 ℃ for 1.5 h,then furnace cooling and air cooling were performed separately.The results indicate that proper post-welded heat treatment improves the ductility of the joint at high temperature.
引用
收藏
页码：732 / 739
页数：8
相关论文
共 50 条
  • [21] SUPERPLASTICITY RESEARCH OF Ti-23Al-17Nb ALLOY SHEET
    Fu Mingjie
    Han Xiuquan
    Wu Wei
    Zhang Jianwei
    ACTA METALLURGICA SINICA, 2014, 50 (08) : 955 - 961
  • [22] Embrittlement of Ti-23Al-17Nb alloy laser welded joint at 650°C
    Song Zhihua
    Wu Aiping
    Wang Guoqing
    Zou Guisheng
    Ren Jialie
    ADVANCED MATERIAL SCIENCE AND TECHNOLOGY, PTS 1 AND 2, 2011, 675-677 : 743 - 746
  • [23] Control of duplex-microstructure and its effect on mechanical properties of Ti-23Al-17Nb alloys
    Zhang, Jianwei
    Zhang, Haishen
    Zhang, Xuecheng
    Liang, Xiaobo
    Cheng, Yunjun
    Li, Shiqiong
    Xiyou Jinshu Cailiao Yu Gongcheng/Rare Metal Materials and Engineering, 2010, 39 (02): : 372 - 376
  • [24] Control of Duplex-Microstructure and Its Effect on Mechanical Properties of Ti-23Al-17Nb Alloys
    Zhang Jianwei
    Zhang Haishen
    Zhang Xuecheng
    Liang Xiaobo
    Cheng Yunjun
    Li Shiqiong
    RARE METAL MATERIALS AND ENGINEERING, 2010, 39 (02) : 372 - 376
  • [25] Effect of post-weld heat treatments on microstructure and mechanical properties of friction welded alloy 718 joints
    Damodaram, R.
    Raman, S. Ganesh Sundara
    Rao, K. Prasad
    MATERIALS & DESIGN, 2014, 53 : 954 - 961
  • [26] Effect of post-weld heat treatment on the microstructure and mechanical properties of the 2205DSS/Q235 laser beam welding joint
    Du, Chengchao
    Wang, Xue
    Luo, Chang
    JOURNAL OF MATERIALS PROCESSING TECHNOLOGY, 2019, 263 : 138 - 150
  • [27] Effect of post-weld heat treatment on 6156 aluminum alloy joint formed by electron beam welding
    Wang, Shaogang
    Xu, Junke
    Wang, Yongpeng
    HIGH TEMPERATURE MATERIALS AND PROCESSES, 2023, 42 (01)
  • [28] Effects of a post-weld heat treatment on the microstructure and mechanical properties of dual-spot laser welded-brazed Ti/Al butt joints
    Li, Peng
    Lei, Zhenglong
    Zhang, Xinrui
    Chen, Yanbin
    JOURNAL OF MANUFACTURING PROCESSES, 2021, 61 : 492 - 506
  • [29] Effect of post-weld heat treatment on microstructure and property of linear friction welded Ti17 titanium alloy joint
    Ma, T. J.
    Li, W. Y.
    Zhong, B.
    Zhang, Y.
    Li, J. L.
    SCIENCE AND TECHNOLOGY OF WELDING AND JOINING, 2012, 17 (03) : 180 - 185
  • [30] Effect of post-weld heat treatment on the microstructure and properties of titanium/304 stainless steel laser welding dissimilar metal joints with copper as the transition layer
    Li, Yun-long
    Di, Hong-shuang
    Wang, Xiao-nan
    Chen, Li-qing
    Li, Tian-xiang
    MATERIALS TODAY COMMUNICATIONS, 2023, 36
12345