Effect of Aging on Fracture Toughness and Stress Corrosion Cracking Resistance of Forged 7475 Aluminum Alloy

被引：0
|
作者：
李红英
机构：
[1] Ministry of Education
[2] Changsha 410083
[3] China Key Lab of Nonferrous Metal Materials Science and Engineering
[4] School of Materials Science and Engineering Central South University
来源：
Journal of Wuhan University of Technology(Materials Science) | 2007年 / 02期
关键词：
7475; alloy; two-stage aging; heat treatment; RRA treatment fracture toughness; stress corrosion;
D O I：
暂无
中图分类号：
TG136.1 []; TG172.9 [其他腐蚀];
学科分类号：
080502 ; 080503 ;
摘要：
The effects of two-stage aging and retrogression and reaging heat treatment on the fracture toughness and stress corrosion cracking resistance of 7475 alloy were studied.The fracture toughness,conductivity and strength of samples of nine groups under duplex aging conditions and three retrogression and reaging heat treatments were also measured.Incorporating the microstructure and property,we found that when the condition of the first order aging kept identical,the fracture toughness and stress corrosion cracking resistance increase with aging time and the second aging temperature.The optimal treatment conditions are (115℃×7h+185℃×13h)among all tested two-stage aging treatments.Although the 7475 alloy treated by RRA method shows the highest strength and its stress corrosion cracking resistance after twenty minutes retrogression can also reach the same level as those by the optimal treatment of(115℃×7h+185℃×13h),the fracture toughness is even low.
引用
收藏
页码：191 / 195
页数：5
相关论文
共 50 条
  • [21] EFFECT OF EXTRUSION PROCESS ON THE STRESS CORROSION CRACKING RESISTANCE OF 7N01 ALUMINUM ALLOY
    Xie, H.
    Yang, Z.
    Ma, Q. -S.
    Meng, W.
    Hu, L.
    Yin, X. -H.
    [J]. JOURNAL OF MINING AND METALLURGY SECTION B-METALLURGY, 2023, 59 (01) : 137 - 146
  • [22] Effect of oxygen on fracture toughness and stress-corrosion cracking of Ti-6211
    Pao, Peter
    Imam, M. Ashraf
    Jones, Harry
    Bayles, Robert
    Feng, Jerry
    [J]. TMS 2008 ANNUAL MEETING SUPPLEMENTAL PROCEEDINGS, VOL 1: MATERIALS PROCESSING AND PROPERTIES, 2008, : 403 - 409
  • [23] MARINE CORROSION STUDIES (EFFECT OF STRESS-CORROSION CRACKING ON FRACTURE TOUGHNESS INDEX OF TITANIUM ALLOYS)
    BROWN, BF
    NEWBEGIN, RL
    [J]. REPORT OF NRL PROGRESS, 1966, (JUL): : 26 - &
  • [24] Corrosion Resistance of 7475-T7351 Aluminum Alloy Plate for Aviation
    [J]. Liu, Ming (mingliu5753@163.com), 1600, Beijing Institute of Aeronautical Materials (BIAM) (45):
  • [25] DIRECTIONAL EFFECTS IN STRESS CORROSION CRACKING OF AN ALUMINUM ALLOY
    UGIANSKY, GM
    SKOLNICK, LP
    STIEFEL, SW
    [J]. CORROSION, 1969, 25 (02) : 77 - &
  • [26] Effects of silicon content on microstructure and stress corrosion cracking resistance of 7050 aluminum alloy
    She, Huan
    Chu, Wei
    Shu, Da
    Wang, Jun
    Sun, Bao-de
    [J]. TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2014, 24 (07) : 2307 - 2313
  • [27] DISCUSSION ON FRACTURE TOUGHNESS AND STRESS-CORROSION PROPERTIES OF ALUMINUM-ALLOY HAND FORGINGS
    SPROWLS, DO
    KAUFMAN, JG
    [J]. JOURNAL OF MATERIALS, 1972, 7 (02): : 263 - &
  • [28] Effect of quenching rate on microstructure and stress corrosion cracking of 7085 aluminum alloy
    Chen Song-yi
    Chen Kang-hua
    Peng Guo-sheng
    Liang Xin
    Chen Xue-hai
    [J]. TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2012, 22 (01) : 47 - 52
  • [29] Effect of Quenching Rate on Stress Corrosion Cracking Susceptibility of 7136 Aluminum Alloy
    Ma Zhimin
    Deng Yunlai
    Liu Jia
    Liu Shengdan
    Liu Honglei
    [J]. ACTA METALLURGICA SINICA, 2022, 58 (09) : 1118 - 1128
  • [30] THE EFFECT OF STRESS CORROSION ON THE FRACTURE TOUGHNESS OF STEEL
    Gajdos, L'ubomir
    Sperl, Martin
    [J]. 25TH DANUBIA-ADRIA SYMPOSIUM ON ADVANCES IN EXPERIMENTAL MECHANICS, 2008, : 73 - 74
12345