Effect of Aging on Fracture Toughness and Stress Corrosion Cracking Resistance of Forged 7475 Aluminum Alloy

被引：0
|
作者：
李红英
机构：
[1] Ministry of Education
[2] Changsha 410083
[3] China Key Lab of Nonferrous Metal Materials Science and Engineering
[4] School of Materials Science and Engineering Central South University
来源：
Journal of Wuhan University of Technology(Materials Science) | 2007年 / 02期
关键词：
7475; alloy; two-stage aging; heat treatment; RRA treatment fracture toughness; stress corrosion;
D O I：
暂无
中图分类号：
TG136.1 []; TG172.9 [其他腐蚀];
学科分类号：
080502 ; 080503 ;
摘要：
The effects of two-stage aging and retrogression and reaging heat treatment on the fracture toughness and stress corrosion cracking resistance of 7475 alloy were studied.The fracture toughness,conductivity and strength of samples of nine groups under duplex aging conditions and three retrogression and reaging heat treatments were also measured.Incorporating the microstructure and property,we found that when the condition of the first order aging kept identical,the fracture toughness and stress corrosion cracking resistance increase with aging time and the second aging temperature.The optimal treatment conditions are (115℃×7h+185℃×13h)among all tested two-stage aging treatments.Although the 7475 alloy treated by RRA method shows the highest strength and its stress corrosion cracking resistance after twenty minutes retrogression can also reach the same level as those by the optimal treatment of(115℃×7h+185℃×13h),the fracture toughness is even low.
引用
收藏
页码：191 / 195
页数：5
相关论文
共 50 条
  • [1] Effect of aging on fracture toughness and stress corrosion cracking resistance of forged 7475 aluminum alloy
    Li, Hongying
    Geng, Jinfeng
    Dong, Xianjuan
    Wang, Changjian
    Zheng, Feng
    [J]. JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION, 2007, 22 (02): : 191 - 195
  • [2] Effect of aging on fracture toughness and stress corrosion cracking resistance of forged 7475 aluminum alloy
    Hongying Li
    Jinfeng Geng
    Xianjuan Dong
    Changjian Wang
    Feng Zheng
    [J]. Journal of Wuhan University of Technology-Mater. Sci. Ed., 2007, 22 : 191 - 195
  • [3] Atmospheric stress corrosion cracking of a superplastic 7475 aluminum alloy
    Tsai, TC
    Chuang, TH
    [J]. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1996, 27 (09): : 2617 - 2627
  • [4] Stress corrosion cracking of superplastically formed 7475 aluminum alloy
    T. C. Tsai
    J. C. Chang
    T. H. Chuang
    [J]. Metallurgical and Materials Transactions A, 1997, 28 : 2113 - 2121
  • [5] Stress corrosion cracking of superplastically formed 7475 aluminum alloy
    Tsai, TC
    Chang, JC
    Chuang, TH
    [J]. METALLURGICAL AND MATERIALS TRANSACTIONS A-PHYSICAL METALLURGY AND MATERIALS SCIENCE, 1997, 28 (10): : 2113 - 2121
  • [6] Effect of heat treatment on stress corrosion cracking, fracture toughness and strength of 7085 aluminum alloy
    Chen, Song-yi
    Chen, Kang-hua
    Dong, Peng-xuan
    Ye, Sheng-ping
    Huang, Lan-ping
    [J]. TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA, 2014, 24 (07) : 2320 - 2325
  • [7] EFFECT OF BENDING STRAIN ON STRESS-CORROSION CRACKING OF 7475 ALUMINUM-ALLOY
    NAGAOKA, K
    NASU, T
    ISANO, T
    IKEDA, K
    [J]. JOURNAL OF THE JAPAN INSTITUTE OF METALS, 1988, 52 (03) : 272 - 278
  • [8] Effect of natural aging time on stress corrosion cracking of aluminum alloy
    [J]. Deng, Yun-Lai (dengylcsu@126.com), 1600, Central South University of Technology (27):
  • [9] FRACTURE TOUGHNESS AND SALT-WATER STRESS-CORROSION-CRACKING RESISTANCE OF TITANIUM ALLOY WELDMENTS
    HUBER, RW
    GOODE, RJ
    JUDY, RW
    [J]. REPORT OF NRL PROGRESS, 1967, (NOV): : 1 - &
  • [10] STRESS CORROSION CRACKING RESISTANCE OF ALUMINUM ALLOY 7000 SERIES AFTER TWO-STEP AGING
    Jegdic, Bore V.
    Bobic, Biljana M.
    Pavlovic, Milos K.
    Alil, Ana B.
    Putic, Slavisa S.
    [J]. CHEMICAL INDUSTRY & CHEMICAL ENGINEERING QUARTERLY, 2015, 21 (02) : 261 - 268
12345